Compositions comprising at least one polymer and at least one metal complex and to electroluminescent devices containing said compositions

ABSTRACT

The present invention relates to compositions comprising at least one polymer which contains triarylamine repeating units, and at least one metal complex, to methods for the production thereof, and the use thereof in electronic devices, especially in organic electroluminescent devices, so-called OLEDs (OLED=Organic Light Emitting Diode). The present invention also relates to organic electroluminescent devices which contain said compositions.

CROSS-REFERENCE TO RELATED APPLICATIONS

This patent application is a U.S. national stage application, filed pursuant to 35 U.S.C. § 371, of PCT Application No. PCT/EP2015/002452, filed Dec. 4, 2015, which claims priority to European Patent Application No. 14004448.8, filed Dec. 30, 2014, both of which are incorporated by reference herein in their entirety.

The present invention relates to compositions comprising at least one polymer and at least one metal complex, to processes for production thereof and to the use thereof in electronic or optoelectronic devices, especially in organic electroluminescent devices, called OLEDs (OLED=organic light-emitting diodes). The present invention also further relates to organic electroluminescent devices comprising these compositions.

In electronic or optoelectronic devices, especially in organic electroluminescent devices (OLEDs), components of various functionality are required. In OLEDs, the different functionalities are normally present in different layers. Reference is made in this case to multilayer OLED systems. The layers in these multilayer OLED systems include charge-injecting layers, for example electron- and hole-injecting layers, charge-transporting layers, for example electron- and hole-conducting layers, and layers containing light-emitting components. These multilayer OLED systems are generally produced by successive layer by layer application.

If two or more layers are applied from solution, it has to be ensured that any layer already applied, after drying, is not destroyed by the subsequent application of the solution for production of the next layer. This can be achieved, for example, by rendering a layer insoluble, for example by crosslinking. Methods of this kind are disclosed, for example, in EP 0 637 899 and WO 96/20253.

Furthermore, it is also necessary to match the functionalities of the individual layers in terms of the material such that very good results, for example in terms of lifetime, efficiency, etc., are achieved. For instance, particularly the layers that directly adjoin an emitting layer, especially the hole-transporting layer (HTL=hole transport layer) have a significant influence on the properties of the adjoining emitting layer.

Known electronic devices and the methods for production thereof have a usable profile of properties. However, there is a constant need to improve the properties of these devices and the methods for production of these devices.

These properties of the devices especially include the energy efficiency with which an electronic device solves the problem defined. In the case of organic light-emitting diodes, the light yield in particular should be sufficiently high that a minimum amount of electrical power has to be applied to achieve a particular luminous flux. In addition, a minimum voltage should also be necessary to achieve a defined luminance. A further particular problem is the lifetime of the electronic devices.

One of the problems addressed by the present invention was therefore that of providing compositions which can firstly be processed as a solution and which secondly lead to an improvement in the properties of the device, especially of the OLED, when used in electronic or optoelectronic devices, preferably in OLEDs, and here especially in the hole injection and/or hole transport layer thereof.

It has been found that, surprisingly, compositions including polymers having repeat triarylamine units and metal complexes, especially when used for production of the hole-injecting layer and/or hole-transporting layer of OLEDs, lead to a distinct lowering of the voltage for achievement of a given luminance, a reduction in the electrical power needed to achieve a particular luminous flux, and an increase in the lifetime of these OLEDs. It has been found here that, surprisingly, the components of the composition, i.e. the polymers and the metal complexes, interact in a synergistic manner without having any adverse effect on other properties. Particular advantages can especially be achieved by using an inventive composition in a hole injection layer.

The present application thus provides a composition comprising at least one polymer and at least one metal complex, which is characterized in that the polymer which has at least one structural unit of the following formula (I):

where

-   Ar¹, Ar² and Ar³ are the same or different at each instance and are     a mono- or polycyclic, aromatic or heteroaromatic ring system which     may be substituted by one or more R radicals; -   R is the same or different at each instance and is H, D, F, Cl, Br,     I, N(R¹)₂, CN, NO₂, Si(R¹)₃, B(OR¹)₂, C(═O)R¹, P(═O)(R¹)₂, S(═O)R¹,     S(═O)₂R¹, OSO₂R¹, a straight-chain alkyl, alkoxy or thioalkoxy group     having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2     to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or     thioalkoxy group having 3 to 40 carbon atoms, each of which may be     substituted by one or more R¹ radicals, where one or more     nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂,     C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S or CONR¹ and where     one or more hydrogen atoms may be replaced by D, F, Cl, Br, I or CN,     or an aromatic or heteroaromatic ring system which has 5 to 60     aromatic ring atoms and may be substituted in each case by one or     more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5     to 60 aromatic ring atoms and may be substituted by one or more R¹     radicals, or an aralkyl or heteroaralkyl group which has 5 to 60     aromatic ring atoms and may be substituted by one or more R¹     radicals, or a diarylamino group, diheteroarylamino group or     arylheteroarylamino group which has 10 to 40 aromatic ring atoms and     may be substituted by one or more R¹ radicals; where two or more R     radicals together may also form a mono- or polycyclic, aliphatic,     aromatic and/or benzofused ring system; -   R¹ is the same or different at each instance and is H, D, F or an     aliphatic hydrocarbyl radical having 1 to 20 carbon atoms, an     aromatic and/or a heteroaromatic hydrocarbyl radical having 5 to 20     carbon atoms, in which one or more hydrogen atoms may also be     replaced by F; where two or more R¹ substituents together may also     form a mono- or polycyclic, aliphatic or aromatic ring system; and     the dotted lines represent bonds to adjacent structural units in the     polymer; and     the metal complex comprises a metal atom of groups 13 to 15 and a     ligand of the structure (L-I):

in which R¹¹ and R¹² may independently be oxygen, sulfur, selenium, NH or NR¹⁴ where R¹⁴ is selected from the group comprising alkyl or aryl and may be bonded to R¹³; and

R¹³ is a straight-chain alkyl, alkoxy or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or thioalkoxy group having 3 to 40 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S or CONR¹ and where one or more hydrogen atoms may be replaced by D, F, Cl, Br, I or CN, or an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and may be substituted by one or more R¹ radicals; where the R¹³ radical may also form a ring system with one or both of the R¹¹ and R¹² radicals, where R¹ may assume the definition detailed above.

Preferably, at least one of the Ar¹, Ar² and Ar³ radicals in formula (I) comprises at least one R substituent having at least 2 carbon atoms, preferably at least 4 and most preferably at least 6 carbon atoms.

Particularly advantageously, this substituent having 2 carbon atoms displays a C—C double bond between these 2 carbon atoms or this substituent having 2 carbon atoms is part of a mono- or polycyclic, aromatic or heteroaromatic ring system having 5 to 60 aromatic ring atoms.

In a first particularly preferred configuration, it may be the case that the Ar³ radical of formula (I) is substituted by Ar⁴ in at least one ortho position, preferably in exactly one of the two ortho positions, based on the position of the nitrogen atom shown in formula (I), where Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted by one or more R radicals, where R may be as defined above, especially for formula (I).

Ar⁴ may be joined to Ar³ either directly, i.e. by a single bond, or else via a linking group X.

The structural unit of the formula (I) may thus preferably have the structure of the following formula (Ia):

where Ar¹, Ar², Ar³, Ar⁴ and R may each be as defined above, q=0, 1, 2, 3, 4, 5 or 6, preferably 0, 1, 2, 3 or 4, X=CR₂, NR, SiR₂, O, S, C═O or P═O, preferably CR₂, NR, O or S, and r=0 or 1, preferably 0.

In the polymeric compounds have preferably 10 to 10 000, more preferably present application, the term “polymer” is understood to mean polymeric compounds, oligomeric compounds and dendrimers. The inventive 10 to 5000 and most preferably 10 to 2000 structural units (i.e. repeat units). The inventive oligomeric compounds preferably have 3 to 9 structural units. The branching factor of the polymers is between 0 (linear polymer, no branching sites) and 1 (fully branched dendrimer).

The polymers usable in accordance with the invention preferably have a molecular weight M_(w) in the range from 1000 to 2 000 000 g/mol, more preferably a molecular weight M_(w) in the range from 10 000 to 1 500 000 g/mol and most preferably a molecular weight M_(w) in the range from 50 000 to 1 000 000 g/mol. The molecular weight M_(w) is determined by means of GPC (=gel permeation chromatography) against an internal polystyrene standard.

The inventive polymers are conjugated, semi-conjugated or non-conjugated polymers. Preference is given to conjugated or semi-conjugated polymers.

According to the invention, the structural units of the formula (I) may be incorporated into the main chain or side chain of the polymer. Preferably, however, the structural units of the formula (I) are incorporated into the main chain of the polymer. In the case of incorporation into the side chain of the polymer, the structural units of the formula (I) may either be mono- or bivalent, meaning that they have either one or two bonds to adjacent structural units in the polymer.

“Conjugated polymers” in the context of the present application are polymers containing mainly sp²-hybridized (or else optionally sp-hybridized) carbon atoms in the main chain, which may also be replaced by correspondingly hybridized heteroatoms. In the simplest case, this means the alternating presence of double and single bonds in the main chain, but polymers having units such as a meta-bonded phenylene, for example, should also be regarded as conjugated polymers in the context of this application. “Mainly” means that defects that occur naturally (involuntarily) and lead to interrupted conjugation do not make the term “conjugated polymer” inapplicable. Conjugated polymers are likewise considered to be polymers having a conjugated main chain and non-conjugated side chains. In addition, the present application likewise refers to conjugation when, for example, arylamine units, arylphosphine units, particular heterocycles (i.e. conjugation via nitrogen, oxygen or sulphur atoms) and/or organometallic complexes (i.e. conjugation by the metal atom) are present in the main chain. The same applies to conjugated dendrimers. In contrast, units such as simple alkyl bridges, (thio)ether, ester, amide or imide linkages, for example, are unambiguously defined as non-conjugated segments.

A semi-conjugated polymer shall be understood in the present application to mean a polymer containing conjugated regions separated from one another by non-conjugated sections, deliberate conjugation breakers (for example spacer groups) or branches, for example in which comparatively long conjugated sections in the main chain are interrupted by non-conjugated sections, or containing comparatively long conjugated sections in the side chains of a polymer non-conjugated in the main chain. Conjugated and semiconjugated polymers may also contain conjugated, semi-conjugated or non-conjugated dendrimers.

The term “dendrimer” in the present application shall be understood to mean a highly branched compound formed from a multifunctional core to which monomers branched in a regular structure are bonded, such that a tree-like structure is obtained. In this case, both the core and the monomers may assume any desired branched structures consisting both of purely organic units and organometallic compounds or coordination compounds. “Dendrimeric” shall generally be understood here as described, for example, by M. Fischer and F. Vögtle (Angew. Chem., Int. Ed. 1999, 38, 885).

The term “structural unit” in the present application is understood to mean a unit which, proceeding from a monomer unit having at least two, preferably two, reactive groups, by a bond-forming reaction, is incorporated into the polymer base skeleton as a portion thereof and is present thus bonded as a repeat unit within the polymer prepared.

The term “mono- or polycyclic aromatic ring system” is understood in the present application to mean an aromatic ring system which has 6 to 60, preferably 6 to 30 and more preferably 6 to 24 aromatic ring atoms and does not necessarily contain only aromatic groups, but in which it is also possible for two or more aromatic units to be interrupted by a short nonaromatic unit (<10% of the atoms other than H, preferably <5% of the atoms other than H), for example an sp³-hybridized carbon atom or oxygen or nitrogen atom, a CO group, etc. For example, systems such as 9,9′-spirobifluorene, 9,9-diarylfluorene and 9,9-dialkylfluorene, for example, shall also be regarded as aromatic ring systems.

The aromatic ring systems may be mono- or polycyclic, meaning that they may have one ring (e.g. phenyl) or two or more rings which may also be fused (e.g. naphthyl) or covalently bonded (e.g. biphenyl), or contain a combination of fused and bonded rings.

Preferred aromatic ring systems are, for example, phenyl, biphenyl, terphenyl, [1,1′:3′,1″] terphenyl-2′-yl, quarterphenyl, naphthyl, anthracene, binaphthyl, phenanthrene, dihydrophenanthrene, pyrene, dihydropyrene, chrysene, perylene, tetracene, pentacene, benzpyrene, fluorene, indene, indenofluorene and spirobifluorene.

The term “mono- or polycyclic heteroaromatic ring system” is understood in the present application to mean an aromatic ring system having 5 to 60, preferably 5 to 30 and more preferably 5 to 24 aromatic ring atoms, where one or more of these atoms is/are a heteroatom. The “mono- or polycyclic heteroaromatic ring system” does not necessarily contain only aromatic groups, but may also be interrupted by a short nonaromatic unit (<10% of the atoms other than H, preferably <5% of the atoms other than H), for example an sp³-hybridized carbon atom or oxygen or nitrogen atom, a CO group, etc.

The heteroaromatic ring systems may be mono- or polycyclic, meaning that they may have one ring or two or more rings which may also be fused or covalently bonded (e.g. pyridylphenyl), or contain a combination of fused and bonded rings. Preference is given to fully conjugated heteroaryl groups.

Preferred heteroaromatic ring systems are, for example, 5-membered rings such as pyrrole, pyrazole, imidazole, 1,2,3-triazole, 1,2,4-triazole, tetrazole, furan, thiophene, selenophene, oxazole, isoxazole, 1,2-thiazole, 1,3-thiazole, 1,2,3-oxadiazole, 1,2,4-oxadiazole, 1,2,5-oxadiazole, 1,3,4-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,5-thiadiazole, 1,3,4-thiadiazole, 6-membered rings such as pyridine, pyridazine, pyrimidine, pyrazine, 1,3,5-triazine, 1,2,4-triazine, 1,2,3-triazine, 1,2,4,5-tetrazine, 1,2,3,4-tetrazine, 1,2,3,5-tetrazine, or groups having several rings, such as carbazole, indenocarbazole, indole, isoindole, indolizine, indazole, benzimidazole, benzotriazole, purine, naphthimidazole, phenanthrimidazole, pyridimidazole, pyrazinimidazole, quinoxalinimidazole, benzoxazole, naphthoxazole, anthroxazole, phenanthroxazole, isoxazole, benzothiazole, benzofuran, isobenzofuran, dibenzofuran, quinoline, isoquinoline, pteridine, benzo-5,6-quinoline, benzo-6,7-quinoline, benzo-7,8-quinoline, benzoisoquinoline, acridine, phenothiazine, phenoxazine, benzopyridazine, benzopyrimidine, quinoxaline, phenazine, naphthyridine, azacarbazole, benzocarboline, phenanthridine, phenanthroline, thieno[2,3b]thiophene, thieno[3,2b]thiophene, dithienothiophene, isobenzothiophene, dibenzothiophene, benzothiadiazothiophene or combinations of these groups.

The mono- or polycyclic, aromatic or heteroaromatic ring system may be unsubstituted or substituted. “Substituted” in the present application means that the mono- or polycyclic, aromatic or heteroaromatic ring system has one or more R substituents.

R is preferably the same or different at each instance and is H, D, F, Cl, Br, I, N(R¹)₂, CN, NO₂, Si(R¹)₃, B(OR¹)₂, C(═O)R¹, P(═O)(R¹)₂, S(═O)R¹, S(═O)₂R¹, OSO₂R¹, a straight-chain alkyl, alkoxy or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or thioalkoxy group having 3 to 40 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S or CONR¹ and where one or more hydrogen atoms may be replaced by D, F, Cl, Br, I or CN, or an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and may be substituted by one or more R¹ radicals; at the same time, two or more R radicals together may also form a mono- or polycyclic, aliphatic, aromatic and/or benzofused ring system.

R is more preferably the same or different at each instance and is H, D, F, Cl, Br, I, N(R¹)₂, Si(R¹)₃, B(OR¹)₂, C(═O)R¹, P(═O)(R¹)₂, a straight-chain alkyl or alkoxy group having 1 to 20 carbon atoms or an alkenyl or alkynyl group having 2 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group having 3 to 20 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═NR¹, P(═O)(R¹), NR¹, O or CONR¹ and where one or more hydrogen atoms may be replaced by F, Cl, Br or I, or an aromatic or heteroaromatic ring system which has 5 to 30 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 30 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 30 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 20 aromatic ring atoms and may be substituted by one or more R¹ radicals; at the same time, two or more R radicals together may also form a mono- or polycyclic, aliphatic, aromatic and/or benzofused ring system.

R is even more preferably the same or different at each instance and is H, a straight-chain alkyl or alkoxy group having 1 to 10 carbon atoms or an alkenyl or alkynyl group having 2 to 10 carbon atoms or a branched or cyclic alkyl or alkoxy group having 3 to 10 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, C═O, C═NR¹, NR¹, O or CONR¹, or an aromatic or heteroaromatic ring system which has 5 to 20 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 20 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 20 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 20 aromatic ring atoms and may be substituted by one or more R¹ radicals; at the same time, two or more R radicals together may also form a mono- or polycyclic, aliphatic, aromatic and/or benzofused ring system.

Preferred alkyl groups having 1 to 10 carbon atoms are depicted in the following table:

R¹ is preferably the same or different at each instance and is H, D, F or an aliphatic hydrocarbyl radical having 1 to 20 carbon atoms, an aromatic and/or a heteroaromatic hydrocarbyl radical having 5 to 20 carbon atoms, in which one or more hydrogen atoms may also be replaced by F; at the same time, two or more R¹ substituents together may also form a mono- or polycyclic, aliphatic or aromatic ring system.

R¹ is more preferably the same or different at each instance and is H, D or an aliphatic hydrocarbyl radical having 1 to 20 carbon atoms, an aromatic and/or a heteroaromatic hydrocarbyl radical having 5 to 20 carbon atoms; at the same time, two or more R¹ substituents together may also form a mono- or polycyclic, aliphatic or aromatic ring system.

R¹ is even more preferably the same or different at each instance and is H or an aliphatic hydrocarbyl radical having 1 to 10 carbon atoms, an aromatic and/or a heteroaromatic hydrocarbyl radical having 5 to 10 carbon atoms.

In a further embodiment of the present invention, the at least one structural unit of the formula (I) in the inventive polymer is characterized in that Ar³ is substituted by Ar⁴ in one of the two ortho positions, and Ar³ is additionally joined to Ar⁴ in the meta position adjacent to the substituted ortho position.

It may additionally be the case that the sum total of the ring atoms of the Ar⁴ radical together with the ring atoms of the Ar³ group bonded to said radical of formulae (Ia) and/or (Ib) is at least 10, preferably at least 12. Preferably, the Ar⁴ radical together with the ring atoms of the Ar³ group bonded to said radical of formulae (Ia) and/or (Ib) does not form a fused ring system. In addition, preferred radicals are Ar⁴ groups having a low condensation level, and so preference is given to monocyclic, aromatic or heteroaromatic ring systems or to polycyclic, aromatic or heteroaromatic ring systems wherein the aromatic or heteroaromatic rings are bonded via groups which minimize or eliminate conjugation of the rings.

The structural unit of the formula (I) may thus preferably have the structure of the following formula (Ib):

where Ar¹, Ar², Ar³, Ar⁴ and R may each be as defined above, m=0, 1, 2, 3 or 4, n=0, 1, 2 or 3, X=CR₂, NR, SiR₂, O, S, C═O or P═O, preferably CR₂, NR, O or S, and s and t are each 0 or 1, where the sum of (s+t)=1 or 2, preferably 1.

In a preferred embodiment, the at least one structural unit of the formula (I) is selected from the structural units of the following formulae (II), (Ill) and (IV):

where Ar¹, Ar², Ar⁴ and R may each be as defined above, m=0, 1, 2, 3 or 4, n=0, 1, 2 or 3, and X=CR₂, NR, SiR₂, O, S, C═O or P═O, preferably CR₂, NR, O or S.

In a particularly preferred embodiment, the at least one structural unit of the formula (II) is selected from the structural unit of the following formula (V):

where Ar¹, Ar², R, m and the dotted lines may each be as defined above for formulae (I) and/or (Ib), and p=0, 1, 2, 3, 4 or 5.

Examples of preferred structural units of the formula (V) are depicted in the following table:

where Ar¹, Ar², R, m, n, p and the dotted lines may each be as defined above for formulae (I), (Ib) and/or (V), and o=0, 1 or 2.

In a further particularly preferred embodiment, the at least one structural unit of the formula (III) is selected from the structural unit of the following formula (VI):

where Ar¹, Ar², R, X, m, n and the dotted lines may each be as defined above for formulae (I) and/or (Ib).

Examples of preferred structural units of the formula (VI) are depicted in the following table:

where Ar¹, Ar², R, m, n and p may each be as defined above for formulae (I), (Ib) and/or (V).

In yet a further particularly preferred embodiment, the at least one structural unit of the formula (IV) is selected from the structural unit of the following formula (VII):

where Ar¹, Ar², R, X, m, n and the dotted lines may each be as defined above for formulae (I) and/or (Ib).

Examples of preferred structural units of the formula (VII) are depicted in the following table:

where Ar¹, Ar², R, m, n, p and the dotted lines may each be as defined above for formulae (I), (Ib) and/or (V).

In a very particularly preferred embodiment, the at least one structural unit of the formula (V) is selected from the structural unit of the following formula (Vj):

where R, m, p and the dotted lines may each be as defined above for formula (V).

Examples of preferred structural units of the formula (Vj) are depicted in the following table:

where R, m, n, p and the dotted lines may each be as defined for formula (V) and o is 0, 1 or 2.

In a further very particularly preferred embodiment, the at least one structural unit of the formula (VI) is selected from the structural unit of the following formula (VIg):

where R, X, m, n and the dotted lines may each be as defined above for formula (VI).

Examples of preferred structural units of the formula (VIg) are depicted in the following table:

where R, m, n, p and the dotted lines may each be as defined above for formulae (V) and/or (VI), and v=1 to 20, preferably 1 to 10.

In yet a further very particularly preferred embodiment, the at least one structural unit of the formula (VII) is selected from the structural unit of the following formula (VIIg):

where R, X, m, n and the dotted lines may each be as defined above for formula (VII).

Examples of preferred structural units of the formula (VIIg) are depicted in the following table:

where R, m and n may each be as defined above for formulae (I) and/or (Ib).

In the formulae (Vj), (VIg) and (VIIg) and their preferred embodiments of the formulae (Vj-1) to (Vj-7), (VIg-1) to (VIg-7) and (VIIg-1) to (VIIg-3), the dotted lines represent the bonds to the adjacent structural units in the polymer. They may independently be arranged identically or differently in the ortho, meta or para positions, preferably identically in the ortho, meta or para position, more preferably in the meta or para position and most preferably in the para position.

In a second preferred configuration of the present invention, it may be the case that the polymer comprises at least one structural unit of the formula (I) selected from the structural unit of the following formula (VIIIa):

or the structural unit of the following formula (VIIIb):

where w=1, 2 or 3, Ar⁵ to Ar⁹ are each the same or different at each instance and are a mono- or polycyclic, aromatic or heteroaromatic ring system which may be substituted by one or more R radicals, where R may be as defined above, especially for formula (I); the dotted lines represent bonds to adjacent structural units in the polymer.

Preferably, at least one of the Ar⁵ to Ar⁹ radicals comprises at least one R substituent having at least 2 carbon atoms, preferably at least 4 and most preferably at least 6 carbon atoms.

Preferably, it may be the case that the structural units of the formulae (VIIIa) and/or (VIIIb) correspond to the structural units of the formula (I).

Preferably, at least one of the Ar⁵ and/or Ar⁸ radicals of formulae (VIIIa) and/or (VIIIb) comprises substituted by Ar⁴ in at least one ortho position, preferably in exactly one of the two ortho positions, based on the position of the nitrogen atom shown in formula (VIIIa) and/or (VIIIb), where Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted by one or more R radicals, where R may be as defined above, especially for formula (I).

It may additionally be the case that the sum total of the ring atoms of the Ar⁴ radical together with the ring atoms of the Ar⁵ or Ar⁸ group bonded to said radical of formulae (VIIIa) and/or (VIIIb) is at least 12. Preferably, the Ar⁴ radical together with the ring atoms of the Ar⁵ or Ar⁸ group bonded to said radical of formulae (VIIIa) and/or (VIIIb) does not form a fused ring system. In addition, preferred radicals are Ar⁴ groups having a low condensation level, and so preference is given to monocyclic, aromatic or heteroaromatic ring systems or to polycyclic, aromatic or heteroaromatic ring systems wherein the aromatic or heteroaromatic rings are bonded via groups which minimize or eliminate conjugation of the rings.

Ar⁴ can be bonded to at least one of the Ar⁵ and/or Ar⁸ radicals of formulae (VIIIa) and/or (VIIIb) either directly, i.e. via a single bond, or else via a linking group X.

The structural unit of the formula (VIIIa) and/or (VIIIb) may thus preferably have the structure of the following formulae (VIIIa-1a), (VIIIa-1b), (VIIIa-1c) and/or (VIIIa-1d):

where Ar⁴, Ar^(y), Ar⁶, Ar⁷, Ar⁸, Ar⁹, X, m, n, r, s, t and R may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

In addition, the structural unit of the formula (VIIIa) and/or (VIIIb) may thus have the structure of the following formulae (VIIIb-a), (VIIIb-b), (VIIIb-c) and/or (VIIIb-d):

where Ar⁴, Ar⁵, Ar⁶, Ar⁷, Ar⁸, Ar⁹, X, m, n, s, t and R may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

In a preferred embodiment, the at least one structural unit of the formula (VIIIa) is selected from the structural units of the following formulae (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and (XVI):

where Ar⁴, Ar^(y), Ar⁶, Ar⁷, Ar⁸, Ar⁹, X, m, n, p, R and the dotted lines may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

In a particularly preferred embodiment, the structural units of the formulae (IX) and (X) are selected from the structural units of the following formulae (IXa) and (Xa):

where Ar⁶, Ar⁷, Ar⁸, Ar⁹, R, m, p and the dotted lines may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (IXa) and (Xa) are depicted in the following table:

where Ar⁶, Ar⁷, Ar⁸, R, m, n, p and the dotted lines may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In a further particularly preferred embodiment, the structural units of the formulae (XI) and (XII) are selected from the structural units of the following formulae (XIa) and (XIIa):

where Ar⁶, Ar⁷, Ar⁸, Ar⁹, R, m, n and X may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (XIa) and (XIIa) are depicted in the following table:

where Ar⁶, Ar⁷, Ar⁸, R, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In another further particularly preferred embodiment, the structural elements of the formulae (XIII) and (XIV) are selected from the structural units of the following formulae (XIIIa) and (XIVa):

where Ar⁶, Ar⁷, Ar⁸, Ar⁹, R, m, n and X may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (XIIIa) and (XIVa) are depicted in the following table:

where Ar⁶, Ar⁷, Ar⁸, R, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In a very particularly preferred embodiment, the structural units of the formulae (IXa) and (Xa) are selected from the structural units of the following formulae (IXb) and (Xb):

where Ar⁹, R, m and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (IXb) and (Xb) are depicted in the following table:

where R, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In a further very particularly preferred embodiment, the structural units of the formulae (XIa) and (XIIa) are selected from the structural units of the following formulae (XIb) and (XIIb):

where Ar⁹, R, X, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (XIb) and (XIIb) are depicted in the following table:

where R, X, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In yet another further very particularly preferred embodiment, the structural units of the formulae (XIIIa) and (XIVa) are selected from the structural units of the following formulae (XIIIb) and (XIVb):

where R, X, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb).

Examples of preferred structural units of the formulae (XIIIb) and (XIVb) are depicted in the following table:

where R, X, m, n and p may each be as defined above, especially for the formulae (I), (Ia), (Ib), (VIIIa) and/or (VIIIb), and o=0, 1 or 2.

In the formulae (IXa) to (XIVa) and (IXb) to (XIVb), the dotted lines represent the bonds to the adjacent structural units in the polymer. They may independently be arranged identically or differently in the ortho, meta or para positions, preferably identically in the ortho, meta or para position, more preferably in the meta or para position and most preferably in the para position.

In a third preferred configuration of the present invention, it may be the case that at least one of the structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV), (XVI) and/or a preferred configuration of these structural units has at least one crosslinkable Q group.

“Crosslinkable Q group” in the context of the present invention means a functional group capable of entering into a reaction and thus forming an insoluble compound. The reaction may be with a further identical Q group, a further different Q group or any other portion of the same or another polymer chain. The crosslinkable group is thus a reactive group. This affords, as a result of the reaction of the crosslinkable group, a correspondingly crosslinked compound. The chemical reaction can also be conducted in the layer, giving rise to an insoluble layer. The crosslinking can usually be promoted by means of heat or by means of UV radiation, microwave radiation, x-radiation or electron beams, optionally in the presence of an initiator. “Insoluble” in the context of the present invention preferably means that the inventive polymer, after the crosslinking reaction, i.e. after the reaction of the crosslinkable groups, has a lower solubility at room temperature in an organic solvent by at least a factor of 3, preferably at least a factor of 10, than that of the corresponding non-crosslinked inventive polymer in the same organic solvent.

At least one crosslinkable group in the present application means that a structural unit has one or more crosslinkable groups. Preferably, a structural unit has exactly one crosslinkable group.

If the structural unit of the formula (I) has a crosslinkable group, it may be bonded to Ar¹, Ar² or Ar³. Preferably, the crosslinkable group is bonded to the monovalently bonded mono- or polycyclic aromatic or heteroaromatic ring system Ar³.

If the structural unit of the formula (VIIIa) or (VIIIb) has a crosslinkable group, it may be bonded to Ar⁵, Ar⁶, Ar⁸ or Ar⁹. Preferably, the crosslinkable group is bonded to one of the monovalently bonded mono- or polycyclic aromatic or heteroaromatic ring systems, i.e. to Ar⁵ or Ar⁸.

Preferred mono- or polycyclic, aromatic or heteroaromatic Ar³ groups in formula (I), Ar⁴ groups in formulae (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI); Ar⁵ and Ar⁸ groups in formulae (VIIIa) and/or (VIIIb), and the preferred embodiments thereof, are as follows:

The R radicals in the formulae E1 to E12 may be as defined for the R radicals in the formula (I). X may be CR₂, NR, SiR₂, O, S, C═O or P═O, preferably CR₂, SiR₂, NR, O or S, where R here too may be as defined for the R radicals in relation to the formula (I). The dotted line represents the bonding site to the adjacent group.

The indices used are defined as follows:

m=0, 1, 2, 3 or 4;

n=0, 1, 2 or 3;

o=0, 1 or 2; and

p=0, 1, 2, 3, 4 or 5.

Preferred mono- or polycyclic, aromatic or heteroaromatic Ar¹ and Ar² groups in formula (I), Ar⁶, Ar⁷ and Ar⁹ groups in formulae (VIIIa) and/or (VIIIb) are as follows:

The R radicals in the formulae M1 to M23 may be as defined for the R radicals in the formula (I). X may be CR₂, NR, SiR₂, O, S, C═O or P═O, preferably CR₂, SiR₂, NR, O or S, where R here too may be as defined for the R radicals in relation to the formula (I). The dotted lines represent the bonding sites to the adjacent groups.

Y may be CR₂, SiR₂, O, S or a straight-chain or branched, alkyl group having 1 to 20 carbon atoms or an alkenyl or alkynyl group having 2 to 20 carbon atoms, each of which may be substituted by one or more R¹ radicals, and where one or more nonadjacent CH₂ groups, CH groups or carbon atoms in the alkyl, alkenyl or alkynyl groups may be replaced by Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S, CONR¹ or an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and may be substituted by one or more R¹ radicals; where the R and R¹ radicals here too may be as defined for the R and R¹ radicals in formula (I).

The indices used are defined as follows:

k=0 or 1;

m=0, 1, 2, 3 or 4;

n=0, 1, 2 or 3;

o=0, 1 or 2; and

q=0, 1, 2, 3, 4, 5 or 6.

Particularly preferred mono- or polycyclic, aromatic or heteroaromatic Ar^(a) groups in formula (I), Ar⁴ groups in formulae (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI); Ar⁵ and Ar⁸ groups in formulae (VIIIa) and/or (VIIIb), and the preferred embodiments thereof, are as follows:

The R radicals in the formulae E1a to E12a may be as defined for the R radicals in formula (I).

The indices used are defined as follows:

o=0 or 1; and

n=0, 1, 2 or 3.

The R radicals in the formulae E1a to E12a may be the same or different at each instance, preferably H or a straight-chain or branched alkyl group having 1 to 12 carbon atoms, preferably 1 to 10 carbon atoms. More preferably, the R radicals in the formulae E1a to E12a are methyl, n-butyl, sec-butyl, tert-butyl, n-hexyl and n-octyl.

Particularly preferred mono- or polycyclic, aromatic or heteroaromatic Ar² and Ar³ groups in formula (I), Ar⁵, Ar⁷ and Ar⁸ groups in formula (IIa), Ar⁴, Ar⁵ and Ar⁸ groups in formula (IIb), and Ar⁹ groups in formula (III) are as follows:

The R radicals in the formulae M1a to M23a may be as defined for the R radicals in formula (I). X may be CR₂ or SiR₂, where R here too may be as defined for the R radicals in formula (I).

Y may be CR₂, SiR₂, O, S or a straight-chain alkyl group having 1 to 10 carbon atoms or an alkenyl or alkynyl group having 2 to 10 carbon atoms, each of which may be substituted by one or more R¹ radicals, and where one or more nonadjacent CH₂ groups, CH groups or carbon atoms in the alkyl, alkenyl or alkynyl groups may be replaced by Si(R¹)₂, C═O, C═NR¹, P(═O)(R¹), NR¹, O, CONR¹ or an aromatic or heteroaromatic ring system which has 5 to 30 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 30 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 30 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 20 aromatic ring atoms and may be substituted by one or more R¹ radicals; where the R and R¹ radicals here too may be as defined for the R and R¹ radicals in formula (I).

The indices used are defined as follows:

k=0 or 1;

o=0, 1 or 2;

n=0, 1, 2 or 3; and

m=0, 1, 2, 3 or 4.

A selection of preferred structural units of the formula (I) is listed in Table 1 below.

TABLE 1 Formula (I) Ar¹ Ar² Ar³ I1 M1 M1 E1 I2 M2 M2 E1 I3 M10 M10 E1 I4 M12 M12 E1 I5 M14 M14 E1 I6 M19 M19 E1 I7 M1 M1 E2 I8 M1 M2 E2 I9 M7 M7 E2 I10 M12 M12 E2 I11 M13 M13 E2 I12 M1 M1 E3 I13 M13 M13 E3 I14 M1 M1 E4 I15 M2 M2 E4 I16 M14 M14 E4 I17 M3 M3 E5 I18 M12 M12 E5 I19 M6 M6 E6 I20 M10 M10 E6 I21 M16 M16 E6 I22 M2 M2 E7 I23 M15 M15 E7 I24 M1 M1 E8 I25 M2 M2 E8 I26 M4 M4 E8 I27 M5 M5 E8 I28 M10 M10 E8 I29 M12 M12 E8 I30 M14 M14 E8 I31 M1 M1 E9 I32 M8 M8 E9 I33 M13 M13 E9 I34 M10 M10 E10 I35 M9 M9 E11 I36 M17 M17 E11 I37 M7 M7 E12 I38 M18 M18 E12 I39 M23 M23 E1 I40 M1 M21 E2 I41 M20 M20 E8 I42 M22 M22 E9

Particularly preferred structural units of the formula (I) are structural units in which Ar³ is selected from the groups of the formulae E1a to E12a and Ar¹ and Ar² are selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar¹ and Ar² are the same.

A selection of particularly preferred structural units of the formula (I) is listed in Table 2 below.

TABLE 2 Formula (I) Ar¹ Ar² Ar³ I1a M1a M1a E1a I2a M2a M2a E1a I2b M2c M2c E1a I3a M10a M10a E1a I4a M12a M12a E1a I5a M14a M14a E1a I7a M1b M1b E2a I7b M1a M1a E2c I8a M1a M2c E2c I9a M7a M7a E2b I10a M12a M12a E2a I11a M13a M13a E2a I12a M1b M1b E3a I13a M13a M13a E3a I14a M1a M1a E4a I15a M2a M2a E4a I15b M2b M2b E4a I16a M14a M14a E4a I17a M3a M3a E5a I18a M12a M12a E5a I19a M6a M6a E6a I20a M10b M10b E6b I22a M2a M2a E7a I24a M1a M1a E8a I24b M1b M1b E8b I24c M1a M1a E8e I24d M1b M1b E8f I25a M2c M2c E8a I25b M2b M2b E8b I25c M2c M2c E8f I26a M4a M4a E8c I27a M5a M5a E8d I28a M10a M10a E8c I29a M12a M12a E8b I30a M14a M14a E8e I31a M1a M1a E9b I32a M8a M8a E9a I33a M13a M13a E9a I34a M10c M10c E10a I36a M17a M17a E11a I37a M7a M7a E12a I39a M23a M23a E1a I39b M23b M23b E1a I40a M1a M21a E2c I40b M1b M21a E2a I41a M20a M20a E8b I41b M20b M20b E8c

Particularly preferred structural units of the formula (VIIIa) are structural units in which Ar⁵ and Ar⁸ are the same or different and are each independently selected from the groups of the formulae E1 to E12 and Ar⁵, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1 to M19, it being particularly preferable when Ar⁵ and Ar⁸, and Ar⁶ and Ar⁷, are the same.

Particularly preferred structural units of the formula (VIIIb) are structural units in which Ar⁵ and Ar⁸ are the same or different and are each independently selected from the groups of the formulae E1 to E12 and Ar⁵, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1 to M19, it being particularly preferable when Ar⁵ and Ar⁸, and Ar⁶ and Ar⁷, are the same.

A selection of preferred structural units of the formulae (VIIIa) and (VIIIb) is listed in Table 3 below.

TABLE 3 Formula (VIIIa) Ar⁵ Ar⁶ Ar⁷ Ar⁸ Ar⁹ Formula (VIIIb) Ar⁵ Ar⁶ Ar⁷ Ar⁸ Ar⁹ VIII1 E1 M1 M1 E1 M1 VIII2 E1 M1 M1 E1 M2 VIII3 E1 M1 M1 E1 M10 VIII4 E1 M1 M1 E1 M13 VIII5 E1 M1 M1 E1 M14 VIII6 E1 M14 M14 E1 M12 VIII7 E2 M1 M1 E2 M2 VIII8 E2 M2 M2 E2 M12 VIII9 E3 M7 M7 E3 M1 VIII10 E3 M10 M10 E3 M16 VIII11 E4 M1 M1 E4 M7 VIII12 E4 M1 M1 E4 M12 VIII13 E4 M2 M2 E4 M14 VIII14 E4 M10 M10 E4 M13 VIII15 E4 M1 M1 E8 M7 VIII16 E5 M2 M13 E5 M13 VIII17 E6 M3 M3 E6 M6 VIII18 E6 M17 M17 E6 M10 VIII19 E7 M5 M5 E7 M4 VIII20 E8 M1 M1 E8 M1 VIII21 E8 M1 M1 E8 M2 VIII22 E8 M1 M1 E8 M12 VIII23 E8 M2 M2 E8 M10 VIII24 E8 M6 M6 E8 M8 VIII25 E8 M10 M10 E8 M7 VIII26 E8 M13 M13 E8 M2 VIII27 E8 M14 M14 E8 M12 VIII28 E9 M1 M1 E9 M2 VIII29 E9 M9 M9 E9 M11 VIII30 E9 M19 M19 E9 M18 VIII31 E10 M1 M1 E10 M4 VIII32 E11 M2 M2 E11 M10 VIII33 E11 M13 M13 E11 M15 VIII34 E12 M7 M7 E12 M14 VIII35 E2 M1 M1 E2 M14 VIII36 E2 M1 M1 E2 M12 VIII37 E8 M1 M1 E8 M20 VIII38 E9 M1 M1 E9 M23

Particularly preferred structural units of the formula (VIIIa) are structural units in which Ar⁵ and Ar⁸ are the same or different and are each independently selected from the groups of the formulae E1a to E12a and Ar⁵, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar⁵ and Ar⁸, and Ar⁶ and Ar⁷, are the same.

Particularly preferred structural units of the formula (VIIIb) are structural units in which Ar⁵ and Ar⁸ are the same or different and are each independently selected from the groups of the formulae E1a to E12a and Ar⁵, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar^(y) and Ar⁸, and Ar⁶ and Ar⁷, are the same.

A selection of particularly preferred structural units of the formula (VIIIa) or (VIIIb) is listed in Table 4 below.

TABLE 4 Formula (VIIIa) Ar⁵ Ar⁶ Ar⁷ Ar⁸ Ar⁹ Formula (VIIIb) Ar⁵ Ar⁶ Ar⁷ Ar⁸ Ar⁹ VIII1a E1a M1a M1a E1a M1a VIII1b E1a M1b M1b E1a M1b VIII2a E1a M1a M1a E1a M2a VIII3a E1a M1a M1a E1a M10a VIII4a E1a M1a M1a E1a M13a VIII4b E1a M1b M1b E1a M13a VIII5a E1a M1a M1a E1a M14a VIII6a E1a M14a M14a E1a M12a VIII7a E2a M1a M1a E2a M2a VIII7b E2c M1a M1a E2c M2a VIII8a E2b M2b M2b E2b M12a VIII9a E3a M7a M7a E3a M1b VIII11a E4a M1b M1b E4a M7a VIII12a E4a M1b M1b E4a M12a VIII13a E4a M2b M2b E4a M14a VIII14a E4a M10a M10a E4a M13a VIII15a E4a M1b M1b E8a M7a VIII16a E5a M2c M13a E5a M13a VIII17a E6a M3a M3a E6a M6a VIII18a E6b M17a M17a E6b M10b VIII19a E7a M5a M5a E7a M4a VIII20a E8f M1a M1a E8f M1a VIII21a E8b M1a M1a E8b M2a VIII21b E8e M1a M1a E8e M2a VIII22a E8b M1b M1b E8b M12a VIII23a E8d M2b M2b E8d M10c VIII24a E8f M6a M6a E8f M8a VIII25a E8a M10a M10a E8a M7a VIII26a E8c M13a M13a E8c M2c VIII27a E8b M14a M14a E8b M12a VIII28a E9a M1a M1a E9a M2a VIII28b E9b M1a M1a E9b M2a VIII31a E10a M1b M1b E10a M4a VIII32a E11a M2c M2c E11a M10c VIII34a E12a M7a M7a E12a M14a VIII35a E2a M1a M1a E2a M14a VIII35b E2c M1a M1a E2c M14a VIII36a E2c M1a M1a E2c M12a VIII37a E8b M1a M1a E8b M20a VIII37b E8e M1a M1a E8e M20b VIII38a E9a M1b M1b E9a M23a VIII38b E9b M1b M1b E9b M23b

As described above, the crosslinkable Q group means a functional group capable of entering into a chemical reaction and thus forming an insoluble polymeric compound. It is generally possible to use any Q groups known for the purpose to the person skilled in the art. The particular function of this group is to join the inventive polymeric compounds to one another by a crosslinking reaction, optionally with further reactive polymeric compounds. This leads to a crosslinked compound or, when the reaction is conducted in a layer, to a crosslinked layer. A crosslinked layer in the context of the present invention is understood to mean a layer obtainable by conducting the crosslinking reaction from a layer of the inventive crosslinkable polymeric compound. The crosslinking reaction can generally be initiated by means of heat and/or by means of UV radiation, microwave radiation, x-radiation or electron beams and/or by the use of free-radical formers, anions, cations, acids and/or photoacids. The presence of catalysts may likewise be advisable or necessary. Preferably, the crosslinking reaction is a reaction for which no initiator and no catalyst need be added.

Crosslinkable Q groups preferred in accordance with the invention are the following groups:

a) Terminal or Cyclic Alkenyl or Terminal Dienyl and Alkynyl Groups:

-   -   Suitable units are those which contain a terminal or cyclic         double bond, a terminal dienyl group or a terminal triple bond,         especially terminal or cyclic alkenyl, terminal dienyl or         terminal alkynyl groups having 2 to 40 carbon atoms, preferably         having 2 to 10 carbon atoms, where individual CH₂ groups and/or         individual hydrogen atoms may also be replaced by the         abovementioned R groups. Additionally suitable are also groups         which are to be regarded as precursors and which are capable of         in situ formation of a double or triple bond.         b) Alkenyloxy, Dienyloxy or Alkynyloxy Groups:     -   Additionally suitable are alkenyloxy, dienyloxy or alkynyloxy         groups, preferably alkenyloxy groups.         c) Acrylic Acid Groups:     -   Additionally suitable are acrylic acid units in the broadest         sense, preferably acrylic esters, acrylamides, methacrylic         esters and methacrylamides. Particular preference is given to         C₁₋₁₀-alkyl acrylate and C₁₋₁₀-alkyl methacrylate.     -   The crosslinking reaction of the groups mentioned above under a)         to c) can be effected via a free-radical, cationic or anionic         mechanism, or else via cycloaddition.     -   It may be advisable to add an appropriate initiator for the         crosslinking reaction. Suitable initiators for the free-radical         crosslinking are, for example, dibenzoyl peroxide, AIBN or         TEMPO. Suitable initiators for the cationic crosslinking are,         for example, AlCl₃, BF₃, triphenylmethyl perchlorate or         tropylium hexachloroantimonate. Suitable initiators for the         anionic crosslinking are bases, especially butyllithium.     -   In a preferred embodiment of the present invention, the         crosslinking, however, is conducted without the addition of an         initiator and is initiated exclusively by thermal means. The         reason for this preference is that the absence of the initiator         prevents contamination of the layer which could lead to         worsening of the device properties.         d) Oxetanes and Oxiranes:     -   A further suitable class of crosslinkable Q groups is that of         oxetanes and oxiranes which crosslink cationically via ring         opening.     -   It may be advisable to add an appropriate initiator for the         crosslinking reaction. Suitable initiators are, for example,         AlCl₃, BF₃, triphenylmethyl perchlorate or tropylium         hexachloroantimonate. It is likewise possible to add photoacids         as initiators.         e) Silanes:     -   Additionally suitable as a class of crosslinkable groups are         silane groups SiR₃ where at least two R groups, preferably all         three R groups, are Cl or an alkoxy group having 1 to 20 carbon         atoms.     -   This group reacts in the presence of water to give an oligo- or         polysiloxane.         f) Cyclobutane Groups

The abovementioned crosslinkable Q groups are generally known to those skilled in the art, as are the suitable reaction conditions which are used for reaction of these groups.

Preferred crosslinkable Q groups include alkenyl groups of the following formula Q1, dienyl groups of the following formula Q2, alkynyl groups of the following formula Q3, alkenyloxy groups of the following formula Q4, dienyloxy groups of the following formula Q5, alkynyloxy groups of the following formula Q6, acrylic acid groups of the following formulae Q7 and Q8, oxetane groups of the following formulae Q9 and Q10, oxirane groups of the following formula Q11 and cyclobutane groups of the following formula Q12:

The R¹¹⁰, R¹²⁰ and R¹³⁰ radicals in the formulae Q1 to Q8 and Q11 are the same or different at each instance and are H or a straight-chain or branched alkyl group having 1 to 6 carbon atoms, preferably 1 to 4 carbon atoms. More preferably, the R¹¹⁰, R¹²⁰ and R¹³⁰ radicals are H, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl or tert-butyl and most preferably H or methyl. The indices used are defined as follows: g=0 to 8; and h=1 to 8.

The dotted bond in the formulae Q1 to Q11 and the dotted bonds in the formula Q12 represent the linkage of the crosslinkable group to the structural units.

The crosslinkable groups of the formulae Q1 to Q12 may be joined directly to the structural unit, or else indirectly, via a further mono- or polycyclic, aromatic or heteroaromatic ring system Ar¹⁰, as shown in the following formulae Q13 to Q24:

where Ar¹⁰ in the formulae Q13 to Q24 may be as defined for the Ar¹ radical described in detail for formula (I). The indices used are defined as follows: g=0 to 8; and h=1 to 8.

Particularly preferred crosslinkable Q groups are as follows:

The indices used are defined as follows: g=0 to 8; and h=1 to 8.

The R¹¹⁰ and R¹²⁰ radicals in the formulae Q7a and Q13a to Q19a are the same or different at each instance and are H or a straight-chain or branched alkyl group having 1 to 6 carbon atoms, preferably 1 to 4 carbon atoms. More preferably, the R¹¹⁰ and R¹²⁰ radicals are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl or tert-butyl and most preferably methyl.

The R¹³⁰ radical in the formulae Q7b and Q19b at each instance is a straight-chain or branched alkyl group having 1 to 6 carbon atoms, preferably 1 to 4 carbon atoms. More preferably, the R¹³⁰ radical is methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl or tert-butyl and most preferably methyl.

Very particularly preferred crosslinkable Q groups are as follows:

In the preferred Q1 to Q24 groups, in the particularly preferred Q1a to Q24a groups and in the very particularly preferred Q1b to Q24c groups, the dotted lines represent the bonds to the structural units. It should be noted in this connection that the Q12, Q12a, Q12b and Q24 groups each have two bonds to two adjacent ring carbon atoms in the structural unit. All the other crosslinkable groups have only one bond to the structural unit.

The structural unit that bears the crosslinkable Q group may, in a first embodiment, be selected from the structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV), (XVI) and/or a preferred configuration of these structural units.

A preferred structural unit that bears the crosslinkable Q group is the following structural unit, derived from the triarylamine units of group 1, of the formula (XVII):

where Ar¹, Ar², Ar³ and the dotted lines may be as defined above, especially in relation to formula (I), and Q is a crosslinkable group.

Examples of preferred structural units of the formula (XVII) are depicted in the following table:

in which Q is a crosslinkable group and the dotted lines may be as defined above, especially in relation to formula (I).

Preferred structural units that bear the crosslinkable Q group are the following structural units, derived from the structural unit of the formula (Ia), of the formulae (XVIIIa1) to (XVIIIa3):

where Ar¹, Ar², Ar³, Ar⁴, R, q, r, X and r may each be as defined above, especially in relation to formula (Ia), Q is a crosslinkable group and the dotted lines may be as defined above, especially in relation to formula (I).

Examples of preferred structural units of the formula (XVIIIa) are depicted in the following table:

where R, m, n, p and the dotted lines may be as defined above, especially in relation to formulae (I) and (Ib), and Q is a crosslinkable group.

Further preferred structural units that bear the crosslinkable Q group are the following structural units, derived from the structural unit of the formula (Ib), of the formulae (XVIIIb1) to (XVIII1b4):

where Ar¹, Ar², Ar³, Ar⁴, R n, X, s and t may each be as defined above, especially in relation to formula (Ib).

Examples of preferred structural units of the formula (XVIIIb) are depicted in the following table:

where R, m, n and p may each be as defined above, especially in relation to formula (Ib), and o=0, 1 or 2.

In the formulae (18g) to (18o), the dotted lines represent possible bonds to the adjacent structural units in the polymer. If two dotted lines are present in the formulae, the structural unit has one or two, preferably two, bond(s) to adjacent structural units.

There follows a detailed description of the attachment of the crosslinkable Q group in relation to the attachment to Ar³, the particularly preferred embodiment. The same statements also apply to Ar⁵ and Ar⁸ in formula (VIIIa) and to Ar⁵ and Ar⁸ in formula (VIIIb).

The preferred crosslinkable Q1 to Q24 groups are preferably bonded to the preferred E1 to E12 groups of Ar³. The particularly preferred Q1a to Q24a groups are preferably bonded to the particularly preferred E1a to E12a groups of Ar³.

Preferred crosslinkable mono- or polycyclic, aromatic or heteroaromatic Ar³ groups in formula (I), Ar⁴ groups in formulae (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI); Ar⁵ and Ar⁸ groups in formulae (VIIIa) and/or (VIIIb), and the preferred embodiments thereof, are as follows:

The R radicals in the formulae VE1 to VE12 may be as defined for the R radicals in the formulae (I) and (II). X may be CR₂, SiR₂, NR, O or S, where R here too may be as defined for the R radicals in the formulae (I) and (II). The indices used are defined as follows:

o=0, 1 or 2;

n=0, 1, 2 or 3;

m=0, 1, 2, 3 or 4; and

p=0, 1, 2, 3, 4 or 5.

Particularly preferred crosslinkable mono- or polycyclic, aromatic or heteroaromatic Ar¹ and Ar² groups in formula (I), Ar⁶, Ar⁷ and Ar⁸ groups in formulae (VIIIa) and/or (VIIIb) are as follows:

The R radicals in the formulae VE1a to VE12a may be as defined for the R radicals in the formula (I). In addition, at least one of the R radicals may also be as defined for Q, i.e. may be a further crosslinkable Q group in the Ar³ groups.

The indices used are defined as follows:

k=0 or 1; and

n=0, 1, 2 or 3.

A selection of preferred crosslinkable structural units of the formula (XVII) is listed in Table 6 below.

TABLE 6 Formula (I) Ar³ Q Ar¹ Ar² XVII 1 VE1 Q1 M1 M1 XVII 2 VE1 Q14 M2 M2 XVII 3 VE1 Q7 M10 M10 XVII 4 VE1 Q2 M12 M12 XVII 5 VE1 Q2 M14 M14 XVII 6 VE1 Q10 M19 M19 XVII 7 VE2 Q13 M1 M1 XVII 8 VE2 Q24 M2 M1 XVII 9 VE2 Q19 M7 M7 XVII 10 VE2 Q2 M12 M12 XVII 11 VE2 Q13 M13 M13 XVII 12 VE3 Q1 M1 M1 XVII 13 VE3 Q14 M13 M13 XVII 14 VE4 Q7 M1 M1 XVII 15 VE4 Q19 M2 M2 XVII 16 VE4 Q24 M14 M14 XVII 17 VE5 Q16 M3 M3 XVII 18 VE5 Q13 M12 M12 XVII 19 VE6 Q9 M6 M6 XVII 20 VE6 Q16 M10 M10 XVII 21 VE6 Q3 M16 M16 XVII 22 VE7 Q9 M2 M2 XVII 23 VE7 Q20 M15 M15 XVII 24 VE8 Q13 M1 M1 XVII 25 VE8 Q19 M2 M2 XVII 26 VE8 Q16 M4 M4 XVII 27 VE8 Q21 M5 M5 XVII 28 VE8 Q2 M10 M10 XVII 29 VE8 Q24 M12 M12 XVII 30 VE8 Q14 M14 M14 XVII 31 VE9 Q4 M1 M1 XVII 32 VE9 Q21 M8 M8 XVII 33 VE9 Q1 M13 M13 XVII 34 VE10 Q9 M10 M10 XVII 35 VE11 Q5 M9 M9 XVII 36 VE11 Q9 M17 M17 XVII 37 VE12 Q1 M7 M7 XVII 38 VE12 Q12 M18 M18 XVII 39 VE1 Q12 M1 M1

Particularly preferred crosslinkable structural units of the formula (XVII) are structural units in which Ar³ is selected from the groups of the formulae VE1a to VE12a, Ar¹ and Ar² are selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar¹ and Ar² are the same, and Q is selected from the Q1a to Q24a groups.

A selection of particularly preferred crosslinkable structural units of the formula (XVII) is listed in Table 7 below.

TABLE 7 Formula (I) Ar³ Q Ar¹ Ar² XVII 1a VE1a Q1a M1a M1a XVII 2a VE1a Q14a M2a M2a XVII 2b VE1a Q14a M2c M2c XVII 3a VE1a Q7a M10a M10a XVII 4a VE1a Q2a M12a M12a XVII 5a VE1a Q2a M14a M14a XVII 7a VE2a Q13a M1b M1b XVII 7b VE2c Q13b M1a M1a XVII 8a VE2c Q24a M2c M1a XVII 9a VE2b Q19b M7a M7a XVII 10a VE2a Q2a M12a M12a XVII 11a VE2a Q13a M13a M13a XVII 12a VE3a Q1a M1b M1b XVII 13a VE3a Q14a M13a M13a XVII 14a VE4a Q7b M1a M1a XVII 15a VE4a Q19a M2a M2a XVII 15b VE4a Q19b M2b M2b XVII 16a VE4a Q24a M14a M14a XVII 17a VE5a Q16a M3a M3a XVII 18a VE5a Q13a M12a M12a XVII 19a VE6a Q9a M6a M6a XVII 20a VE6b Q16a M10b M10b XVII 22a VE7a Q9a M2a M2a XVII 24a VE8a Q13a M1a M1a XVII 24b VE8b Q13a M1b M1b XVII 24c VE8e Q13a M1a M1a XVII 24d VE8f Q13a M1b M1b XVII 25a VE8a Q19b M2c M2c XVII 25b VE8b Q19b M2b M2b XVII 25c VE8f Q19a M2c M2c XVII 26a VE8c Q16a M4a M4a XVII 27a VE8d Q2la M5a M5a XVII 28a VE8c Q2a M10a M10a XVII 29a VE8b Q24a M12a M12a XVII 30a VE8e Q14a M14a M14a XVII 31a VE9b Q4a M1a M1a XVII 32a VE9a Q21a M8a M8a XVII 33a VE9a Q1a M13a M13a XVII 34a VE10a Q9a M10c M10c XVII 36a VE11a Q9a M17a M17a XVII 37a VE12a Q1a M7a M7a XVII 39a VE1a Q12a M1a M1a

Preferred crosslinkable structural units of the formula (VIIIva)

are structural units in which Ar⁵ is selected from the groups of the formulae E1 to E12, Ar⁶, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1 to M19, it being particularly preferable when Ar⁶ and Ar⁷ are the same, Ar⁸ is selected from the VE1 to VE12 groups and Q is selected from the Q1 to Q24 groups.

Preferred crosslinkable structural units of the formula (VIIIvb)

are structural units in which Ar⁵ is selected from the groups of the formulae E1 to E12, Ar⁶, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1 to M19, it being particularly preferable when Ar⁴ and Ar⁵ are the same, Ar⁸ is selected from the groups of the formulae VE1 to VE12 and Q is selected from the Q1 to Q24 groups.

A selection of preferred structural units of the formula (VIIIva) or (VIIIvb) is listed in Table 8 below.

TABLE 8 Formula (VIIIva) Ar⁵ Ar⁸ Q Ar⁶ Ar⁷ Ar⁹ Formula (VIIIvb) Ar⁵ Ar⁸ Q Ar⁶ Ar⁷ Ar⁹ IIv1 E1 VE1 Q1 M1 M1 M1 IIv2 E1 VE1 Q13 M1 M1 M2 IIv3 E1 VE1 Q19 M1 M1 M10 IIv4 E1 VE1 Q2 M1 M1 M13 IIv5 E1 VE1 Q13 M1 M1 M14 IIv6 E1 VE1 Q24 M14 M14 M12 IIv7 E2 VE2 Q13 M1 M1 M2 IIv8 E2 VE2 Q7 M2 M2 M12 IIv9 E3 VE3 Q4 M7 M7 M1 IIv10 E3 VE3 Q22 M10 M10 M16 IIv11 E4 VE4 Q4 M1 M1 M7 IIv12 E4 VE4 Q1 M1 M1 M12 IIv13 E4 VE4 Q14 M2 M2 M14 IIv14 E4 VE4 Q24 M10 M10 M13 IIv15 E4 VE8 Q19 M1 M1 M7 IIv16 E5 VE5 Q14 M2 M13 M13 IIv17 E6 VE6 Q21 M3 M3 M6 IIv18 E6 VE6 Q16 M17 M17 M10 IIv19 E7 VE7 Q9 M5 M5 M4 IIv20 E8 VE8 Q14 M1 M1 M1 IIv21 E8 VE8 Q19 M1 M1 M2 IIv22 E8 VE8 Q1 M1 M1 M12 IIv23 E8 VE8 Q9 M2 M2 M10 IIv24 E8 VE8 Q21 M6 M6 M8 IIv25 E8 VE8 Q7 M10 M10 M7 IIv26 E8 VE8 Q13 M13 M13 M2 IIv27 E8 VE8 Q7 M14 M14 M12 IIv28 E9 VE9 Q24 M1 M1 M2 IIv29 E9 VE9 Q22 M9 M9 M11 IIv30 E9 VE9 Q12 M19 M19 M18 IIv31 E10 VE10 Q9 M1 M1 M4 IIv32 E11 VE11 Q16 M2 M2 M10 IIv33 E11 VE11 Q8 M13 M13 M15 IIv34 E12 VE12 Q14 M7 M7 M14 IIv35 E1 VE1 Q12 M1 M1 M2 IIv36 E2 VE2 Q1 M1 M1 M14

Particularly preferred structural units of the formula (VIIIva) are structural units in which Ar⁵ is selected from the groups of the formulae E1a to E12a, Ar⁶, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar⁶ and Ar⁷ are the same, Ar⁸ is selected from the groups of the formulae VE1a to VE12a and Q is selected from the Q1a to Q24a groups.

Particularly preferred structural units of the formula (VIIIvb) are structural units in which Ar⁵ is selected from the groups of the formulae E1a to E12a, Ar⁶, Ar⁷ and Ar⁹ are the same or different and are each independently selected from the groups of the formulae M1a to M17a, it being particularly preferable when Ar⁶ and Ar⁷ are the same, Ar⁸ is selected from the groups of the formulae VE1a to VE12a and Q is selected from the Q1a to Q24a groups.

A selection of particularly preferred structural units of the formula (VIIIva) or (VIIIvb) is listed in Table 9 below.

TABLE 9 Formula (VIIIa) Ar⁵ Ar⁸ Q Ar⁶ Ar⁷ Ar⁹ Formula (VIIIb) Ar⁵ Ar⁸ Q Ar⁶ Ar⁷ Ar⁹ IIv1a E1a VE1a Q1a M1a M1a M1a IIv1b E1a VE1a Q1a M1b M1b M1b IIv2a E1a VE1a Q13a M1a M1a M2a IIv3a E1a VE1a Q19b M1a M1a M10a IIv4a E1a VE1a Q2a M1a M1a M13a IIv4b E1a VE1a Q2a M1b M1b M13a IIv5a E1a VE1a Q13a M1a M1a M14a IIv6a E1a VE1a Q24a M14a M14a M12a IIv7a E2a VE2a Q13a M1a M1a M2a IIv7b E2c VE2c Q13a M1a M1a M2a IIv8a E2b VE2b Q7b M2b M2b M12a IIv9a E3a VE3a Q4a M7a M7a M1b IIv11a E4a VE4a Q4a M1b M1b M7a IIv12a E4a VE4a Q1a M1b M1b M12a IIv13a E4a VE4a Q14a M2b M2b M14a IIv14a E4a VE4a Q24a M10a M10a M13a IIv15a E4a VE8a Q19b M1b M1b M7a IIv16a E5a VE5a Q14a M2c M13a M13a IIv17a E6a VE6a Q21a M3a M3a M6a IIv18a E6b VE6b Q16a M17a M17a M10b IIv19a E7a VE7a Q9a M5a M5a M4a IIv20a E8f VE8f Q14a M1a M1a M1a IIv21a E8b VE8b Q19a M1a M1a M2a IIv21b E8e VE8e Q19b M1a M1a M2a IIv22a E8b VE8b Q1a M1b M1b M12a IIv23a E8d VE8d Q9a M2b M2b M10c IIv24a E8f VE8f Q21a M6a M6a M8a IIv25a E8a VE8a Q7a M10a M10a M7a IIv26a E8c VE8c Q13a M13a M13a M2c IIv27a E8b VE8b Q7a M14a M14a M12a IIv28a E9a VE9a Q24a M1a M1a M2a IIv28b E9b VE9b Q24a M1a M1a M2a IIv31a E10a VE10a Q9a M1b M1b M4a IIv32a E11a VE11a Q16a M2c M2c M10c IIv34a E12a VE12a Q14a M7a M7a M14a IIv35a E1a VE1a Q12a M1a M1a M2a IIv36a E2a VE2a Q1a M1a M1a M14a

The proportion of structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) in the polymer is in the range from 1 to 100 mol %, preferably in the range from 25 to 100 mol %, more preferably in the range from 50 to 95 mol %, based on 100 mol % of all copolymerized monomers present as structural units in the polymer.

In a first preferred embodiment, the inventive polymer contains only one structural unit of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) or (XVI), i.e. the proportion thereof in the polymer is 100 mol %. In this case, the inventive polymer is a homopolymer.

In a second preferred embodiment, the proportion of structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) in the polymer is in the range from 50 to 95 mol %, more preferably in the range from 60 to 95 mol %, based on 100 mol % of all the copolymerizable monomers present as structural units in the polymer, i.e. the inventive polymer has, as well as one or more structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), further structural units other than the structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI).

In a third preferred embodiment, the proportion of structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) in the polymer is in the range from 5 to 50 mol %, more preferably in the range from 25 to 50 mol %, based on 100 mol % of all the copolymerizable monomers present as structural units in the polymer, i.e. the inventive polymer has, as well as one or more structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), further structural units other than the structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI).

The proportion of crosslinkable structural units in the polymer may preferably be in the range from 0.01 to 50 mol %, preferably in the range from 0.1 to 30 mol %, more preferably in the range from 0.5 to 25 mol % and most preferably in the range from 1 to 20 mol %, based on 100 mol % of all the copolymerized monomers present as structural units in the polymer.

These structural units that are different from the structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) include those as disclosed and listed comprehensively in WO 02/077060 A1 and in WO 2005/014689 A2. These are considered to form part of the present invention by reference.

Preferably, the polymer may contain at least one further structural unit of the following formula (XIX) other than the structural units of the formulae (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI): —Ar¹¹—  (XIX) where Ar¹¹ is a mono- or polycyclic, aromatic or heteroaromatic ring system which may be substituted by one or more R radicals, where R may be as defined in formula (I).

Preferred structural units of the following formula (XIX) are structural units in which Ar¹¹ is selected from the groups of the formulae M1 to M23, as listed in Table 10 below.

TABLE 10 Formula (XIX) Ar¹¹ XIX1 M1 XIX2 M2 XIX3 M3 XIX4 M4 XIX5 M5 XIX6 M6 XIX7 M7 XIX8 M8 XIX9 M9 XIX10 M10 XIX11 M11 XIX12 M12 XIX13 M13 XIX14 M14 XIX15 M15 XIX16 M16 XIX17 M17 XIX18 M18 XIX19 M19 XIX20 M20 XIX21 M21 XIX22 M22 XIX23 M23

Particularly preferred structural units of the formula (XIX) are structural units in which Ar¹¹ is selected from the groups of the formulae M1a to M23a, as listed in Table 11 below.

TABLE 11 Formula (XIX) Ar¹¹ XIX1a M1a XIX1b M1b XIX2a M2a XIX2b M2b XIX2c M2c XIX3a M3a XIX4a M4a XIX5a M5a XIX6a M6a XIX7a M7a XIX8a M8a XIX10a M10a XIX10b M10b XIX10c M10c XIX12a M12a XIX13a M13a XIX14a M14a XIX17a M17a XIX20a M20a XIX20b M20b XIX20c M20c XIX21a M21a XIX21b M21b XIX22a M22a XIX22b M22b XIX23a M23a XIX23b M23b

The further structural units may come, for example, from the following classes:

-   Group 1: units which influence the hole injection and/or hole     transport properties of the polymers; -   Group 2: units which influence the electron injection and/or     electron transport properties of the polymers; -   Group 3: units having combinations of individual units of group 1     and group 2; -   Group 4: units which alter the emission characteristics in such a     way that electrophosphorescence rather than electrofluorescence is     obtainable; -   Group 5: units which improve the transition from the singlet to the     triplet state; -   Group 6: units which affect the emission colour of the resulting     polymers; -   Group 7: units which are typically used as polymer backbone; -   Group 8: units which affect the film morphology and/or the     rheological properties of the resulting polymers.

Preferred inventive polymers are those in which at least one structural unit has charge transport properties, i.e. those which contain the units from groups 1 and/or 2.

Structural units from group 1 having hole injection and/or hole transport properties are, for example, triarylamine, benzidine, tetraaryl-para-phenylenediamine, triarylphosphine, phenothiazine, phenoxazine, dihydrophenazine, thianthrene, dibenzo-para-dioxin, phenoxathiine, carbazole, azulene, thiophene, pyrrole and furan derivatives and further O-, S- or N-containing heterocycles.

Preferred structural units from group 1 are the structural units of the following formulae (1a) to (1q):

where R, m, n and o may each be as defined above.

In the formulae (1a) to (1q), the dotted lines represent possible bonds to the adjacent structural units in the polymer. If two dotted lines are present in the formulae, the structural unit has one or two, preferably two, bond(s) to adjacent structural units. If three dotted lines are present in the formulae, the structural unit has one, two or three, preferably two, bond(s) to adjacent structural units. If four dotted lines are present in the formulae, the structural unit has one, two, three or four, preferably two, bond(s) to adjacent structural units. They may independently be arranged, identically or differently, in the ortho, meta or para positions.

Structural units from group 2 having electron injection and/or electron transport properties are, for example, pyridine, pyrimidine, pyridazine, pyrazine, oxadiazole, quinoline, quinoxaline, anthracene, benzanthracene, pyrene, perylene, benzimidazole, triazine, ketone, phosphine oxide and phenazine derivatives, but also triarylboranes and further O-, S- or N-containing heterocycles.

It may be preferable when the inventive polymers contain units from group 3 in which structures which increase hole mobility and which increase electron mobility (i.e. units from group 1 and 2) are bonded directly to one another, or structures which increase both hole mobility and electron mobility are present. Some of these units may serve as emitters and shift the emission colour into the green, yellow or red. The use thereof is thus suitable, for example, for the creation of other emission colours from originally blue-emitting polymers.

Structural units of group 4 are those which can emit light with high efficiency from the triplet state even at room temperature, i.e. exhibit electrophosphorescence rather than electrofluorescence, which frequently brings about an increase in energy efficiency. Suitable for this purpose, first of all, are compounds containing heavy atoms having an atomic number of more than 36. Preferred compounds are those which contain d or f transition metals, which fulfil the abovementioned condition. Particular preference is given here to corresponding structural units containing elements of groups 8 to 10 (Ru, Os, Rh, Ir, Pd, Pt). Useful structural units here for the polymers usable in accordance with the invention include, for example, various complexes as described, for example, in WO 02/068435 A1, WO 02/081488 A1, EP 1239526 A2 and WO 2004/026886 A2. Corresponding monomers are described in WO 02/068435 A1 and in WO 2005/042548 A1.

Structural units of group 5 are those which improve the transition from the singlet to the triplet state and which, used in association with the structural elements of group 4, improve the phosphorescence properties of these structural elements. Useful units for this purpose are especially carbazole and bridged carbazole dimer units, as described, for example, in WO 2004/070772 A2 and WO 2004/113468 A1. Additionally useful for this purpose are ketones, phosphine oxides, sulphoxides, sulphones, silane derivatives and similar compounds, as described, for example, in WO 2005/040302 A1.

Structural units of group 6 are, as well as those mentioned above, those which include at least one further aromatic structure or another conjugated structure which are not among the abovementioned groups, i.e. which have only little effect on the charge carrier mobilities, which are not organometallic complexes or which have no effect on the singlet-triplet transition. Structural elements of this kind can affect the emission colour of the resulting polymers. According to the unit, they can therefore also be used as emitters. Preference is given to aromatic structures having 6 to 40 carbon atoms or else tolane, stilbene or bisstyrylarylene derivatives which may each be substituted by one or more R radicals. Particular preference is given to the incorporation of 1,4- or 9,10-anthrylene, 1,6-, 2,7- or 4,9-pyrenylene, 3,9- or 3,10-perylenylene, 4,4′-tolanylene, 4,4′-stilbenylene, benzothiadiazole and corresponding oxygen derivatives, quinoxaline, phenothiazine, phenoxazine, dihydrophenazine, bis(thiophenyl)arylene, oligo(thiophenylene), phenazine, rubrene, pentacene or perylene derivatives which are preferably substituted, or preferably conjugated push-pull systems (systems substituted by donor and acceptor substituents) or systems such as squarines or quinacridones which are preferably substituted.

Structural units of group 7 are units including aromatic structures having 6 to 40 carbon atoms, which are typically used as the polymer backbone. These are, for example, 4,5-dihydropyrene derivatives, 4,5,9,10-tetrahydropyrene derivatives, fluorene derivatives, 9,9′-spirobifluorene derivatives, phenanthrene derivatives, 9,10-dihydrophenanthrene derivatives, 5,7-dihydrodibenzooxepine derivatives and cis- and trans-indenofluorene derivatives, but also 1,2-, 1,3- or 1,4-phenylene, 1,2-, 1,3- or 1,4-naphthylene, 2,2′-, 3,3′- or 4,4′-biphenylylene, 2,2″-, 3,3″- or 4,4″-terphenylylene, 2,2′-, 3,3′- or 4,4′-bi-1,1′-naphthylylene or 2,2′″-, 3,3′″- or 4,4′″-quarterphenylylene derivatives.

Preferred structural units from group 7 are the structural units of the following formulae (7a) to (7o):

where R, m, n, o and p may each be as defined above.

In the formulae (7a) to (7o), the dotted lines represent possible bonds to the adjacent structural units in the polymer. If two dotted lines are present in the formulae, the structural unit has one or two, preferably two, bond(s) to adjacent structural units. If four or more dotted lines are present in the formulae (Formulae (7g), (7h) and (7j)), the structural units have one, two, three or four, preferably two, bond(s) to adjacent structural units. They may independently be arranged, identically or differently, in the ortho, meta or para positions.

Structural units of group 8 are those which affect the film morphology and/or the rheological properties of the polymers, for example siloxanes, alkyl chains or fluorinated groups, but also particularly stiff or flexible units, liquid crystal-forming units or crosslinkable groups.

Preference is given to inventive polymers which simultaneously, as well as structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), additionally contain one or more units selected from groups 1 to 8. It may likewise be preferable when more than one further structural unit from one group is simultaneously present.

Preference is given here to inventive polymers which, as well as at least one structural unit of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), also contain units from group 7.

It is likewise preferable when the polymers usable in accordance with the invention contain units which improve charge transport or charge injection, i.e. units from group 1 and/or 2.

It is additionally particularly preferable when the polymers usable in accordance with the invention contain structural units from group 7 and units from group 1 and/or 2.

The polymers usable in accordance with the invention are either homopolymers of structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) or copolymers. The polymers usable in accordance with the invention may be linear or branched, preferably linear. Inventive copolymers may, as well as one or more structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), potentially contain one or more further structural units from the above-detailed groups 1 to 8.

The inventive copolymers may have random, alternating or block structures, or else have two or more of these structures in alternation. More preferably, the inventive copolymers have random or alternating structures. More preferably, the copolymers are random or alternating copolymers. The way in which copolymers having block structures are obtainable and which further structural elements are particularly preferred for the purpose is described in detail, for example, in WO 2005/014688 A2. This is incorporated into the present application by reference. It should likewise be emphasized once again at this point that the polymer may also have dendritic structures.

In a particularly preferred embodiment of the present invention, the polymers usable in accordance with the invention contain, as well as one or more structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) where Ar³ radical of formula (I) is substituted by Ar⁴ in at least one ortho position, preferably in one of the two ortho positions, based on the position of the nitrogen atom shown in formula (I), or at least one of the Ar⁵ and/or Ar⁸ radical of formulae (VIIIa) and/or (VIIIb) is substituted by Ar⁴ in at least one ortho position, preferably in one of the two ortho positions, based on the position of the nitrogen atom shown in formula (VIIIa) and/or (VIIIb), and optionally further structural units selected from the abovementioned groups 1 to 8, at least one, preferably one, structural unit having a crosslinkable Q group.

In addition, the structural unit bearing the crosslinkable Q group, in a second embodiment, may be selected from the structural units disclosed in groups 1 to 8.

A further preferred structural unit that may bear the crosslinkable Q group is the following structural unit, derived from group 7, of the formula (XX):

where Ar¹ may be as defined in relation to the structural unit of the formula (I).

Examples of preferred structural units of the formula (XX) are depicted in the following table:

The polymers usable in accordance with the invention, containing structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI), are generally prepared by polymerization of one or more monomer types, of which at least one monomer leads, in the polymer, to structural units of the formula (I), (Ia), (Ib), (II), (III), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI). Suitable polymerization reactions are known to those skilled in the art and are described in the literature. Particularly suitable and preferred polymerization reactions which lead to C—C and C—N bonds are as follows:

(A) SUZUKI polymerization;

(B) YAMAMOTO polymerization;

(C) STILLE polymerization;

(D) HECK polymerization;

(E) NEGISHI polymerization;

(F) SONOGASHIRA polymerization;

(G) HIYAMA polymerization; and

(H) HARTWIG-BUCHWALD polymerization.

How the polymerization can be conducted by these methods and how the polymers can then be separated from the reaction medium and purified is known to those skilled in the art and is described in detail in the literature, for example in WO 03/048225 A2, WO 2004/037887 A2 and WO 2004/037887 A2.

The C—C couplings are preferably selected from the groups of SUZUKI coupling, YAMAMOTO coupling and STILLE coupling; the C—N coupling is preferably a coupling according to HARTWIG-BUCHWALD.

For synthesis of the polymers usable in accordance with the invention, it is possible to use the corresponding monomers of the formula (MI)

where Ar¹, Ar² and Ar³ may be as defined in relation to the structural unit of the formula (I).

The monomers of the formula (MI) which lead to structural units of the formula (I) in the inventive polymers are compounds which have corresponding substitution and have suitable functionalities at two positions that allow incorporation of this monomer unit into the polymer. These monomers of the formula (MI) thus likewise form part of the subject-matter of the present invention. The Y group is the same or different and is a leaving group suitable for a polymerization reaction, such that the incorporation of the monomer units into polymeric compounds is enabled. Preferably, Y is a chemical functionality which is the same or different and is selected from the class of the halogens, O-tosylates, O-triflates, O-sulphonates, boric esters, partly fluorinated silyl groups, diazonium groups and organotin compounds.

Corresponding monomers for preparation of structural units of the formulae (VIIIa) and/or (VIIIb) correspondingly arise through replacement of the dotted lines by leaving groups Y as defined for formula (MI).

The basic structure of the monomer compounds can be functionalized by standard methods, for example by Friedel-Crafts alkylation or acylation. In addition, the basic structure can be halogenated by standard organic chemistry methods. The halogenated compounds can optionally be converted further in additional functionalization steps. For example, the halogenated compounds can be used either directly or after conversion to a boronic acid derivative or an organotin derivative as starting materials for the conversion to polymers, oligomers or dendrimers.

Said methods are merely a selection from the reactions known to those skilled in the art, who are able to use these, without exercising inventive skill, to synthesize the inventive compounds.

The polymers usable in accordance with the invention can be used as a pure substance, or else as a mixture together with any further polymeric, oligomeric, dendritic or low molecular weight substances. A low molecular weight substance is understood in the present invention to mean compounds having a molecular weight in the range from 100 to 3000 g/mol, preferably 200 to 2000 g/mol. These further substances can, for example, improve the electronic properties or emit themselves. A mixture refers above and below to a mixture comprising at least one polymeric component. In this way, it is possible to produce one or more polymer layers consisting of a mixture (blend) of one or more inventive polymers having a structural unit of the formula (I), (Ia), (Ib), (II), (Ill), (IV), (V), (VI), (VII), (VIIIa), (VIIIb), (IX), (X), (XI), (XII), (XIII), (XIV), (XV) and/or (XVI) and optionally one or more further polymers with one or more low molecular weight substances.

The inventive compositions comprise at least one metal complex, where the metal complex comprises a metal atom of groups 13 to 15 and a ligand of the structure

in which R¹¹ and R¹² may independently be oxygen, sulfur, selenium, NH or NR¹⁴ where R¹⁴ is selected from the group comprising alkyl or aryl having preferably 1 to 40, more preferably 1 to 20 carbon atoms and most preferably 1 to 12 carbon atoms and may be bonded to R¹³; and

R¹³ is a straight-chain alkyl, alkoxy or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or thioalkoxy group having 3 to 40 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S or CONR¹ and where one or more hydrogen atoms may be replaced by D, F, Cl, Br, I or CN, or an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and may be substituted by one or more R¹ radicals; where the R¹³ radical may also form a ring system with one or both of the R¹¹ and R¹² radicals, where R¹ may assume the definition detailed above.

R¹³ is a straight-chain alkyl, alkoxy or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or thioalkoxy group having 3 to 40 carbon atoms, each of which may be substituted by one or more R¹ radicals, where one or more nonadjacent CH₂ groups may be replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S or CONR¹ and where one or more hydrogen atoms may be replaced by D, F, Cl, Br, I or CN, or an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and may be substituted in each case by one or more R¹ radicals, or an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and may be substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and may be substituted by one or more R¹ radicals; where the R¹³ radical may also form a ring system with one or both of the R¹² and R¹² radicals, where R¹ may assume the definition detailed above.

The metal complex may preferably have a p-dopant effect.

In the context of the present invention, the term “p-dopant” encompasses or means especially materials that have Lewis acidity and/or are capable of forming complexes with the matrix material in which these materials (even if only in a formal sense) have Lewis acidity.

It may preferably be the case that the R¹³ radical in formula (L-I) is selected from the group comprising alkyl, long-chain alkyl, alkoxy, long-chain alkoxy, cycloalkyl, haloalkyl, aryl, arylene, halogenaryl, heteroaryl, heteroarylene, heterocycloalkylene, heterocycloalkyl, haloheteroaryl, alkenyl, haloalkenyl, alkynyl, haloalkynyl, ketoaryl, haloketoaryl, ketoheteroaryl, ketoalkyl, haloketoalkyl, ketoalkenyl, haloketoalkenyl, preferably having 1 to 40 and more preferably 1 to 20 carbon atoms, where, in the case of suitable radicals, one or more nonadjacent CH₂ groups may independently be replaced by —O—, —S—, —NH—, —NR—, —SiR₂—, —CO—, —COO—, —OCO—, —OCO—O—, —SO₂—, —S—CO—, —CO—S—, —CR═CR— or —C≡C—, in such a way that oxygen and/or sulfur atoms are not bonded directly to one another, and are likewise optionally replaced by aryl or heteroaryl preferably containing 1 to 30 carbon atoms (terminal CH₃ groups are regarded as CH₂ groups in the sense of CH₂—H), where R may assume the definition detailed for formula (I).

Long-chain alkyl groups, especially with regard to the description of the R¹¹, R¹² and R¹³ radicals of formula (L-I), preferably have 5 to 20 carbon atoms. Alkyl groups that are not given the attribute “long-chain” may especially, with regard to the description of the R¹¹, R¹² and R¹³ radicals of formula (L-I), have preferably 1 to 10 and more preferably 1 to 4 carbon atoms. The description and definition, especially of the preferred groups detailed in the context of the formula (L-I) can be found, inter alia, in WO 2013/182389 A2, the disclosure of this document here being incorporated by reference into the description of the present application.

The term “main group metal complex of groups 13 to 15” is understood to mean the metals of groups 13 to 15 according to IUPAC, i.e. aluminum, gallium, indium, silicon, germanium, tin, lead, thallium, arsenic, antimony, bismuth or mixtures thereof. Preference is given to the metals of groups 14 and 15, i.e. silicon, germanium, tin, lead, arsenic, antimony, bismuth, more preferably tin and/or bismuth, most preferably bismuth.

In a further-preferred embodiment of the present invention, the metal atom of the metal complex for use in accordance with the invention may be selected from the group comprising bismuth, tin and mixtures thereof, particular preference being given to bismuth.

In a preferred embodiment, the metal complex is a mono- or bi- or polynuclear metal complex. More particularly, the metal complex in the solid state may be in the form of a polynuclear metal complex.

In a preferred embodiment, at least one of the ligands L is in a bridging arrangement between two metals.

In a preferred embodiment, the metal complex has the empirical formula M₂L₄ (with M=metal and L=ligand), where both the metals and the individual ligands may independently be selected according to the above definition.

It may also be the case that the metal complex has the structure ML_(m) where M=metal atom, L=ligand and m=1 to 10 and, if m>1, all L are independent of one another. These metal complexes are especially preferred in the case of tin and bismuth; in this case, m is preferably m=2 for tin or 2, 4, and 3 or 5 for bismuth, according to the oxidation state.

In an alternative embodiment of the invention, the metal complex has the structure ML₂L_(n) with M=metal, L=ligand, as defined above, and L′=a ligand nonidentical to L, selected from the group of aryl, heteroaryl, haloaryl and haloheteroaryl, where n may be from 0 to 3 and, if n>1, each L′ is selected independently of the others. These metal complexes are preferred especially in the case of tin and bismuth; in this case, n=2 for tin or 1 or 3 for bismuth, according to the oxidation state, and n=0 are preferred.

More preferably, the main group metal complex contains bismuth. Particular preference is given here to bismuth-main group metal complexes:

Of the oxidation state II, which, without being bound by theory, may have a paddle-wheel structure as a function of the ligands chosen.

Of the oxidation state III (ML_(n)=3), which, without being bound by theory, do not have a paddle-wheel structure. These compounds in the solid-state are generally in mono- to polynuclear form.

Of the oxidation state V, in which, in a particular embodiment the main group metal complex of bismuth in the V oxidation state may have the structure described in detail in WO 2013/182389 A2.

In a further configuration of the present invention, it is possible to use a metal complex in which the R¹³ radical detailed in formula (L-I) has at least one substituent selected from halogen, pseudohalogen, —CN, —NO₂.

It is advantageously possible to use a metal complex in which the R¹³ radical detailed in formula (L-I) conforms to one of the formulae (R¹³-I), (R¹³-II) and (R¹³-III):

in which the Y¹ to Y⁷ groups are each independently selected from the group comprising C—F, C—CF₃, C—NO₂, C—CN, C-halogen, C-pseudohalogen or N and the dotted line represents the attachment site.

In a preferred embodiment, R¹³ is selected from the group comprising halogenated, preferably perhalogenated and/or pseudohalogenated pteridines, isopteridines, naphthyridines, quinoxalines, azaquinoxalines.

It may also be the case that R¹³ has or consists of one or more of the following structures:

where the dotted line indicates the attachment site.

In a preferred embodiment, the metal complex (without the presence of matrix material) is Lewis-acidic, meaning that it acts as an electron pair acceptor. This has been found to be particularly preferable for interaction with the matrix materials.

In a preferred embodiment, the metal complex (without the presence of matrix material) has at least one unoccupied or partly accessible coordination site. This has likewise been found to be particularly preferable for interaction with the matrix materials.

In a preferred embodiment, R¹³ is haloalkyl, more preferably perfluoroalkyl having 1 to 8 carbons, preferably 1 to 4 carbon atoms, haloaryl, more preferably perfluoroaryl, haloalkylaryl, more preferably (per)fluoroalkylaryl and haloheteroaryl, more preferably perfluoroheteroaryl, where these groups may preferably have 6 to 20 carbon atoms.

It may further be the case that the metal complex comprises a ligand L selected from the group of the unsubstituted, partly fluorinated and perfluorinated organic carboxylic acids.

Further ligands L cited by way of example are preferably fluorinated benzoic acids, for example 2-(trifluoromethyl)benzoic acid; 3,5-difluorobenzoic acid; 3-hydroxy-2,4,6-triiodobenzoic acid; 3-fluoro-4-methylbenzoic acid; 3-(trifluoromethoxy)benzoic acid; 4-(trifluoromethoxy)benzoic acid; 4-chloro-2,5-difluorobenzoic acid; 2-chloro-4,5-difluorobenzoic acid; 2,4,5-trifluorobenzoic acid; 2-fluorobenzoic acid; 4-fluorobenzoic acid; 2,3,4-trifluorobenzoic acid; 2,3,5-trifluorobenzoic acid; 2,3-difluorobenzoic acid; 2,4-bis(trifluoromethyl)benzoic acid; 2,4-difluorobenzoic acid; 2,5-difluorobenzoic acid; 2,6-bis(trifluoromethyl)benzoic acid; 2,6-difluorobenzoic acid; 2-chloro-6-fluorobenzoic acid; 2-fluoro-4-(trifluoromethyl)benzoic acid; 2-fluoro-5-(trifluoromethyl)benzoic acid; 2-fluoro-6-(trifluoromethyl)benzoic acid; 3,4,5-trifluorobenzoic acid; 3,4-difluorobenzoic acid; 3,5-bis(trifluoromethyl)benzoic acid; 3-(trifluoromethyl)benzoic acid; 3-chloro-4-fluorobenzoic acid; 3-fluoro-5-(trifluoromethyl)benzoic acid; 3-fluorobenzoic acid; 4-fluoro-2-(trifluoro-methyl)benzoic acid; 4-fluoro-3-(trifluoromethyl)benzoic acid; 5-fluoro-2-methylbenzoic acid; 2-(trifluoromethoxy)benzoic acid; 2,3,5-trichlorobenzoic acid; 4-(trifluoromethyl)benzoic acid; pentafluorobenzoic acid; 2,3,4,5-tetrafluorobenzoic acid, fluorinated or nonfluorinated phenylacetic acid, for example 2-fluorophenylacetic acid; 3-fluorophenylacetic acid; 4-fluorophenylacetic acid; 2,3-difluorophenylacetic acid; 2,4-difluorophenylacetic acid; 2,6-difluorophenylacetic acid; 3,4-difluorophenylacetic acid; 3,5-difluorophenylacetic acid; pentafluorophenylacetic acid; 2-chloro-6-fluorophenylacetic acid; 2-chloro-3,6-difluorophenylacetic acid; 3-chloro-2,6-difluorophenylacetic acid; 3-chloro-4-fluorophenylacetic acid; 5-chloro-2-fluorophenylacetic acid; 2,3,4-trifluorophenylacetic acid; 2,3,5-trifluorophenyl-acetic acid; 2,3,6-trifluorophenylacetic acid; 2,4,5-trifluorophenylacetic acid; 2,4,6-trifluorophenylacetic acid; 3,4,5-trifluorophenylacetic acid; 3-chloro-2-fluorophenylacetic acid; α-fluorophenylacetic acid; 4-chloro-2-fluorophenyl-acetic acid; 2-chloro-4-fluorophenylacetic acid; α,α-difluorophenylacetic acid; ethyl 2,2-difluoro-2-phenylacetate; and fluorinated or nonfluorinated acetic acid, for example methyl trifluoroacetate; allyl trifluoroacetate; ethyl trifluoroacetate; isopropyl trifluoroacetate; 2,2,2-trifluoroethyl trifluoroacetate; difluoroacetic acid; trifluoroacetic acid; methyl chlorodifluoroacetate; ethyl bromodifluoroacetate; chlorodifluoroacetic acid; ethyl chlorofluoroacetate; ethyl difluoroacetate; (3-chlorophenyl)difluoroacetic acid; (3,5-difluoro-phenyl)difluoroacetic acid; (4-butylphenyl)difluoroacetic acid; (4-tert-butyl-phenyl)difluoroacetic acid; (3,4-dimethylphenyl)difluoroacetic acid; (3-chloro-4-fluorophenyl)difluoroacetic acid; (4-chlorophenyl)difluoroacetic acid; 2-biphenyl-3′,5′-difluoroacetic acid; 3-biphenyl-3′,5′-difluoroacetic acid; 4-biphenyl-3′,5′-difluoroacetic acid; 2-biphenyl-3′,4′-difluoroacetic acid; 3-biphenyl-3′,4′-difluoroacetic acid; 4-biphenyl-3′,4′-difluoroacetic acid and 2,2-difluoropropionic acid or the higher homologs thereof. If the ligands L have acidic groups, the groups may be in deprotonated form in a preferred embodiment.

Particularly preferred metal complexes include Bi(O₂CCF₃)₃, Bi(O₂CC₆H₂(2,3,4-F₃))₃ and bismuth tris(pentafluorobenzoate).

The proportion of metal complex for use in accordance with the invention in a composition of the present invention may be within a wide range. Advantageously, it is possible to use a composition having a weight ratio of polymer for use in accordance with the invention to metal complex for use in accordance with the invention in the range from 1000:1 to 1:2, preferably 400:1 to 1:1, more preferably in the range from 100:1 to 3:2, most preferably in the range from 20:1 to 2:1. The proportion of metal complex for use in accordance with the invention may preferably be 0.1% to 70% by weight, more preferably 0.25% to 50% by weight, even more preferably 1% to 40% by weight and especially preferably 5% to 30% by weight, based on the sum total of polymer and metal complex. Use of a greater or lesser proportion of metal complex is possible, but the efficiency of the composition, of the functional layers obtainable therefrom or of the optoelectronic components comprising these layers decreases unexpectedly in this case. The proportion of metal complex for use in accordance with the invention may preferably be 0.1% to 70% by weight, more preferably 0.25% to 50% by weight, even more preferably 0.5% to 40% by weight and especially preferably 5% to 30% by weight, based on the weight of the composition. The proportion of polymer for use in accordance with the invention may preferably be 30% to 99.9% by weight, more preferably 50% to 99.75% by weight, even more preferably 60% to 99.5% by weight and especially preferably 70% to 95% by weight, based on the weight of the composition. The percentages by weight are based here on metal complexes or polymers having the essential features detailed above. Other metal complexes or polymers are not taken into account in these weight figures.

The present invention further provides a process for producing an inventive composition, which is characterized in that a polymer having structural units of the formula (I) is contacted with a metal complex comprising a metal atom of groups 13 to 15 and a ligand of the structure (L-I).

The way in which the metal complex is contacted with the polymer is uncritical in this context. For example, a solution of a polymer may be mixed with a solution of a metal complex. In addition, a solid polymer can be contacted with a solution of a metal complex. Also, a solid metal complex can be introduced into a polymer solution. Also, a gaseous metal complex can be deposited onto solid polymer. Preference is given to producing a solution of a polymer and a metal complex.

The present invention further provides solutions and formulations composed of one or more inventive compositions. The way in which such solutions can be prepared is known to those skilled in the art and is described, for example, in WO 02/072714 A1, WO 03/019694 A2 and the literature cited therein.

These solutions can be used in order to produce thin polymer layers, for example by surface coating methods (e.g. spin-coating) or by printing methods (e.g. inkjet printing).

Polymers containing structural units having a crosslinkable Q group are particularly suitable for producing films or coatings, especially for producing structured coatings, for example by thermal or light-induced in situ polymerization and in situ crosslinking, for example in situ UV photopolymerization or photopatterning. It is possible here to use either corresponding polymers in pure form or else formulations or mixtures of these polymers as described above. These can be used with or without addition of solvents and/or binders. Suitable materials, processes and apparatuses for the above-described methods are described, for example, in WO 2005/083812 A2. Possible binders are, for example, polystyrene, polycarbonate, poly(meth)acrylates, polyacrylates, polyvinyl butyral and similar optoelectronically neutral polymers.

Suitable and preferred solvents are, for example, toluene, anisole, o-, m- or p-xylene, methyl benzoate, mesitylene, tetralin, veratrole, THF, methyl-THF, THP, chlorobenzene, dioxane, phenoxytoluene, especially 3-phenoxytoluene, (−)-fenchone, 1,2,3,5-tetramethylbenzene, 1,2,4,5-tetramethylbenzene, 1-methylnaphthalene, 2-methylbenzothiazole, 2-phenoxyethanol, 2-pyrrolidinone, 3-methylanisole, 4-methylanisole, 3,4-dimethylanisole, 3,5-dimethylanisole, acetophenone, α-terpineol, benzothiazole, butyl benzoate, cumene, cyclohexanol, cyclohexanone, cyclohexylbenzene, decalin, dodecylbenzene, ethyl benzoate, indane, methyl benzoate, NMP, p-cymene, phenetole, 1,4-diisopropylbenzene, dibenzyl ether, diethylene glycol butyl methyl ether, triethylene glycol butyl methyl ether, diethylene glycol dibutyl ether, triethylene glycol dimethyl ether, diethylene glycol monobutyl ether, tripropylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, 2-isopropylnaphthalene, pentylbenzene, hexylbenzene, heptylbenzene, octylbenzene, 1,1-bis(3,4-dimethylphenyl)ethane or mixtures of these solvents. Preferred solvents are especially ethers and/or esters.

The present invention thus further provides for the use of an inventive composition, comprising a polymer containing structural units having a crosslinkable Q group, for preparation of a crosslinked polymer. The crosslinkable group, which is more preferably a vinyl group or alkenyl group, is preferably incorporated into the polymer by the WITTIG reaction or a WITTIG-like reaction. If the crosslinkable group is a vinyl group or alkenyl group, the crosslinking can take place via free-radical or ionic polymerization, which can be induced thermally or by radiation. Preference is given to free-radical polymerization which is induced thermally, preferably at temperatures of less than 250° C., more preferably at temperatures of less than 230° C.

The crosslinked polymers prepared by the process according to the invention are insoluble in all standard solvents. In this way, it is possible to produce defined layer thicknesses which are not dissolved or partly dissolved again by the application of subsequent layers.

Preferably, the inventive composition can be produced prior to crosslinking of the polymer. Accordingly, for example, a polymer layer produced on a substrate or another layer can be contacted prior to crosslinking with a metal complex usable in accordance with the invention. More preferably, an inventive composition can be applied from solution to a substrate or another layer and optionally crosslinked.

The present invention thus also relates to a composition comprising a crosslinked polymer obtainable by the aforementioned process. The crosslinked polymer is—as described above—preferably produced in the form of a crosslinked polymer layer. Because of the insolubility of the crosslinked polymer in all solvents, a further layer can be applied from a solvent to the surface of such a crosslinked polymer layer by the above-described techniques.

The present invention also encompasses what are called hybrid devices in which one or more layers which are processed from solution and layers which are produced by vapour deposition of low molecular weight substances may occur.

The inventive compositions can be used in electronic or optoelectronic devices or for production thereof.

The present invention thus further provides for the use of the inventive compositions in electronic or optoelectronic devices, preferably in organic electroluminescent devices (OLEDs), organic field-effect transistors (OFETs), organic integrated circuits (O-ICs), organic thin-film transistors (TFTs), organic solar cells (O-SCs), organic laser diodes (O-laser), organic photovoltaic (OPV) elements or devices or organic photoreceptors (OPCs), more preferably in organic electroluminescent devices (OLEDs).

In the case of the aforementioned hybrid device, in conjunction with organic electroluminescent devices, reference is made to combined PLED/SMOLED (polymeric light-emitting diode/small molecule organic light-emitting diode) systems.

The way in which OLEDS can be produced is known to those skilled in the art and is described in detail, for example, as a general process in WO 2004/070772 A2, which has to be adapted appropriately to the individual case.

As described above, the inventive compositions are very particularly suitable as electroluminescent materials in OLEDs or displays produced in this way.

Electroluminescent materials in the context of the present invention are considered to mean materials which can find use as the active layer. “Active layer” means that the layer is capable of emitting light on application of an electrical field (light-emitting layer) and/or that it improves the injection and/or transport of the positive and/or negative charges (charge injection or charge transport layer).

The present invention therefore preferably also provides for the use of the inventive compositions in OLEDs, especially as electroluminescent material.

The present invention further provides electronic or optoelectronic components, preferably organic electroluminescent devices (OLEDs), organic field-effect transistors (OFETs), organic integrated circuits (O-ICs), organic thin-film transistors (TFTs), organic solar cells (O-SCs), organic laser diodes (O-laser), organic photovoltaic (OPV) elements or devices and organic photoreceptors (OPCs), more preferably organic electroluminescent devices, having one or more active layers, wherein at least one of these active layers comprises one or more inventive compositions. The active layer may, for example, be a light-emitting layer, a charge transport layer and/or a charge injection layer.

More preferably, the active layer may comprise a composition of the present invention comprising a crosslinked polymer.

In the present application text and also in the examples that follow hereinafter, the main aim is the use of the inventive compositions in relation to OLEDs and corresponding displays. In spite of this restriction of the description, it is possible for the person skilled in the art, without exercising further inventive skill, to utilize the inventive compositions as semiconductors for the further above-described uses in other electronic devices as well.

The examples which follow are intended to illustrate the invention without restricting it. More particularly, the features, properties and advantages that are described therein for the defined compounds that form the basis of the example in question are also applicable to other compounds that are not referred to in detail but are covered by the scope of protection of the claims, unless the opposite is stated elsewhere.

WORKING EXAMPLES

Part A: Synthesis of the Monomers

The monomers for production of the polymers of the inventive compositions are already described in the prior art, are commercially available or are prepared according to a literature method, and are summarized in the following table:

Monomer Structure Synthesis according to M1

WO 2010/097155 A1 M2

WO 99/048160 A1 M3

Macromolecules 2000, 33, 2016-2020 M4

WO 2013/156130 M5

WO 2013/156130 M6

WO 2013/156130 M7

WO 2013/156130 (analogously to Mo14) M8

J. Mater. Chem., 2012, 22, 7945-7953 M9

Chem. Eur. J. 2006, 12, 4351-4361 Part B: Synthesis of the Polymers

The comparative polymer V1 and the inventive polymers P1 to P8 are prepared by SUZUKI coupling by the process described in WO 2010/097155 from the monomers disclosed in Part A.

The polymers V1 and P1 to P8 prepared in this way contain the structural units, after elimination of the leaving groups, in the percentages reported in Table B1 (percentages=mol %). In the case of the polymers which are prepared from monomers having aldehyde groups, the latter are converted to crosslinkable vinyl groups after the polymerization by WITTIG reaction by the process described in WO 2010/097155. The polymers listed correspondingly in Table B1 and used in Part C thus have crosslinkable vinyl groups rather than the aldehyde groups originally present.

The palladium and bromine contents of the polymers are determined by ICP-MS. The values determined are below 10 ppm.

The molecular weights Mw and the polydispersities D are determined by means of gel permeation chromatography (GPC) (model: Agilent HPLC System Series 1100, column: PL-RapidH from Polymer Laboratories; solvent: THF with 0.12% by volume of o-dichlorobenzene; detection: UV and refractive index; temperature: 40° C.). Calibration is effected with polystyrene standards.

The results are collated in Table B1.

TABLE B1 Molecular weight Polymers Monomers M_(w) (g/mol) Polydispersity V1 M8 50% M9 50% 315 000 2.8 P1 M4 50% M3 50% 339 000 3.1 P2 M4 40% M3 50% M1 10% 328 000 2.9 P3 M4 50% M6 50% 275 000 3.2 P4 M4 40% M6 50% M1 10% 123 000 3.3 P5 M4 40% M3 50% M5 10% 300 000 2.7 P6 M4 40% M7 50% M1 10% 100 000 4.5 P7 M2 50% M3 50% 438 000 3.3 P8 M2 40% M1 10% M3 50% 417 000 3.1 Part C: Dopants

The dopant for production of the inventive compositions is already described in the prior art and is prepared according to a literature method.

Dopant Structure Synthesis according to D1

WO 2013/182389 Part D: Device Examples

The inventive composition, composed of polymer and metal complex, can be processed from solution and leads, compared to vacuum-processed OLEDs, to much more easily producible OLEDs having properties that are nevertheless good.

Whether the crosslinkable variants of the inventive compositions (comprising crosslinkable polymers) after crosslinking give rise to a completely insoluble layer is tested analogously to WO 2010/097155.

Table D1 lists the remaining layer thickness of the original 20 nm after the washing operation described in WO 2010/097155. If there is no decrease in the layer thickness, the composition of polymer and metal complex is insoluble and hence the crosslinking is sufficient.

TABLE D1 Check of the residual layer thickness of the original 20 nm after the wash test Mass ratio of Residual layer thickness after wash Metal polymer:metal test (in nm) Polymer complex complex Crosslinking at 220° C. V1 D1 85:15 3.5 P2 D1 85:15 20 P4 D1 85:15 20 P6 D1 85:15 20 P8 D1 85:15 20

As can be inferred from Table D1, the composition comprising comparative polymer V1 which does not bear any crosslinking group hardly crosslinks at all at 220° C. The mixtures with the inventive polymers P2, P4, P6 and P8 crosslink completely at 220° C.

There are already many descriptions of the production of such solution-based OLEDs in the literature, for example in WO 2004/037887 and WO 2010/097155. The process is matched to the circumstances described hereinafter (variation in layer thickness, materials).

The inventive polymers are used in three different layer sequences:

Structure A is as follows:

-   -   substrate,     -   ITO (50 nm),     -   hole injection layer (HIL) (200 nm),     -   cathode.

Structure B is as follows:

-   -   substrate,     -   ITO (50 nm),     -   HIL (20 nm),     -   hole transport layer (HTL) (40 nm),     -   emission layer (EML) (30 nm),     -   electron transport layer (ETL) (20 nm),     -   cathode.

Structure C is as follows:

-   -   substrate,     -   ITO (50 nm),     -   HIL (20 nm),     -   HTL (20 nm),     -   EML (60 nm),     -   hole blocker layer (HBL) (10 nm),     -   ETL (40 nm),     -   cathode.

Substrates used are glass plates coated with structured ITO (indium tin oxide) of thickness 50 nm. The hole injection, hole transport and emission layers are applied to these coated glass plates.

The hole injection layers used are the inventive compositions, composed of polymer and metal complex, and comparative mixtures, each dissolved in the solvent mixture anisole:xylene (2:1). The typical solids content of such solutions is about 8 to 35 g/l when layer thicknesses between 20 nm and 200 nm are to be achieved by means of spin-coating. The layers are spun on in an inert gas atmosphere, argon in the present case, and baked at 180° C. or 220° C. for 60 minutes.

The hole transport layers in structure C are processed from toluene. The typical solids content of such solutions is about 5 g/l when layer thicknesses of 20 nm are to be achieved by means of spin-coating. The layers are spun on in an inert gas atmosphere, argon in the present case, and baked at 180° C. or 220° C. for 60 minutes.

In structure B, the hole transport layer is formed by thermal evaporation in a vacuum chamber. The materials used in the present case are shown in Table D2.

TABLE D2 Structural formulae of the in the hole-transporting materials processed from vacuum

HT1

The emission layer is always composed of at least one matrix material (host material) and an emitting dopant (emitter). In addition, compositions composed of a plurality of matrix materials and co-dopants may occur. Details given in such a form as H1 (92%):dopant (8%) mean here that the material H1 is present in the emission layer in a proportion by weight of 92% and the dopant in a proportion by weight of 8%. The mixture for the emission layer is dissolved in toluene for structure C. The typical solids content of such solutions is about 18 g/l when, as here, the layer thickness of 60 nm which is typical of a device is to be achieved by means of spin-coating. The layers are spun on in an inert gas atmosphere, argon in the present case, and baked at 180° C. for 10 minutes. In structure B, the emission layer is formed by thermal evaporation in a vacuum chamber. This layer may consist of more than one material, the materials being added to one another by co-evaporation in a particular proportion by volume. Details given in such a form as H3:dopant (95%:5%) mean here that the H3 and dopant materials are present in the layer in a proportion by volume of 95%:5%.

The materials used in the present case are shown in Table D3.

TABLE D3 Structural formulae of the materials used in the emission layer

M1

M2

M3

TEG

SEB

The materials for the hole blocker layer and electron transport layer are likewise applied by thermal vapour deposition in a vacuum chamber and are shown in Table D4. The hole blocker layer consists of ETM1. The electron transport layer consists of the two materials ETM1 and ETM2, which are added to one another by co-evaporation in a proportion by volume of 50% each.

TABLE D4 HBL and ETL materials used

ETM1

ETM2

The cathode is formed by the thermal evaporation of an aluminium layer of thickness 100 nm.

The exact structure of the OLEDs can be found in Table D5. The HTL column lists the polymer used, and the temperature at which the layer is baked and optionally crosslinked.

TABLE D5 Structure of the OLEDs HIL Mass ratio of HTL Metal polymer:metal T T EML Example Structure Polymer complex complex [° C.] Polymer [° C.] Composition D1 B P7 D1 85:15 180 — — M3 95%; SEB 5% D2 C P8 D1 85:15 180 P2 180 M1 30%; M2 55%; TEG 15% D3 A P1 — — 180 — — — D4 A P1 D1 85:15 180 — — — D5 A P3 — — 180 — — — D6 A P3 D1 85:15 180 — — — D7 B P3 D1 85:15 180 — — M3 95%; SEB 5% D8 B P1 D1 85:15 180 — — M3 95%; SEB 5% D9 C P2 D1 85:15 180 P2 180 M1 30%; M2 55%; TEG 15% D10 C P4 D1 85:15 220 P2 180 M1 30%; M2 55%; TEG 15% D11 B V1 D1 85:15 180 — — M3 95%; SEB 5%

The OLEDs are characterized in a standard manner. For this purpose, the electroluminescence spectra, current-voltage-luminance characteristics (IUL characteristics) assuming Lambertian radiation characteristics and, in the case of structures B and C, the (operating) lifetime are determined. The IUL characteristics are used to determine parameters such as the operating voltage (in V) and the external quantum efficiency (in %) at a particular brightness. LD80 @ 1000 cd/m² is the lifetime until the OLED, given a starting brightness of 1000 cd/m², has dropped to 80% of the starting intensity, i.e. to 800 cd/m².

The properties of the different OLEDs are summarized in Tables D6 a and b. Examples D11 and D12 are comparative examples; all the other examples show properties of inventive OLEDs.

Tables D6a and D6b:

Properties of the OLEDs

TABLE D6a Voltage at 1 mA/cm² Example [V] D3 6 D4 1.2 D5 3.2 D6 0.4

TABLE D6b Efficiency at Voltage at LD80 at 1000 cd/m² 1000 cd/m² 1000 cd/m² Example % EQE [V] [h] D1 8.1 4.4 205 D2 16.5 4.9 195 D7 7.9 4.5 266 D8 8.2 4.3 305 D9 16.5 4.9 215 D10 16.3 4.5 240 D11 8.1 4.4 108

Table D6 a shows that the voltages of components made from inventive mixtures (polymer and metal complex) are significantly lower than their equivalents without metal complex. The inventive mixtures are thus suitable as hole injection materials which lower the operating voltage of the OLED.

Table D6 b shows that the use of the inventive mixtures leads to an improvement in lifetime over the prior art. 

The invention claimed is:
 1. A composition comprising at least one polymer and at least one metal complex, wherein the polymer comprises at least one structural unit of formula (I):

wherein Ar¹, Ar² and Ar³ are the same or different in each instance and are a mono- or polycyclic, aromatic or heteroaromatic ring system optionally substituted by one or more R radicals; R is the same or different in each instance and is H, D, F, Cl, Br, I, N(R¹)₂, CN, NO₂, Si(R¹)₃, B(OR¹)₂, C(═O)R¹, P(═O)(R¹)₂, S(═O)R¹, S(═O)₂R¹, OSO₂R¹, a straight-chain alkyl, alkoxy, or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy, or thioalkoxy group having 3 to 40 carbon atoms, each of which is optionally substituted by one or more R¹ radicals, wherein one or more nonadjacent CH₂ groups are optionally replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S, or CONR¹ and wherein one or more hydrogen atoms are optionally replaced by D, F, Cl, Br, I, or CN, an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted in each case by one or more R¹ radicals, an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group, or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and is optionally substituted by one or more R¹ radicals; an wherein two or more R radicals together optionally define a mono- or polycyclic, aliphatic, aromatic and/or benzofused ring system; R¹ is the same or different in each instance and is H, D, F or an aliphatic, aromatic and/or heteroaromatic hydrocarbyl radical having 1 to 20 carbon atoms, wherein one or more hydrogen atoms are optionally replaced by F; and wherein two or more R¹ substituents together optionally define a mono- or polycyclic, aliphatic or aromatic ring system; and the dotted lines denote bonds to adjacent structural units in the polymer; the metal complex comprises an atom selected from the group consisting of silicon, germanium, tin, lead, arsenic, antimony, and bismuth and a ligand of structure (L-I):

wherein R¹¹ and R¹² may independently be oxygen, sulfur, selenium, NH, or NR¹⁴, wherein R¹⁴ is selected from the group comprising alkyl or aryl and may be bonded to R¹³; and R¹³ is a straight-chain alkyl, alkoxy, or thioalkoxy group having 1 to 40 carbon atoms or an alkenyl or alkynyl group having 2 to 40 carbon atoms or a branched or cyclic alkyl, alkoxy or thioalkoxy group having 3 to 40 carbon atoms, each of which are optionally substituted by one or more R¹ radicals, wherein one or more nonadjacent CH₂ groups are optionally replaced by R¹C═CR¹, C≡C, Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR¹, O, S, or CONR¹ and wherein one or more hydrogen atoms are optionally replaced by D, F, Cl, Br, I, or CN, an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and are optionally substituted in each case by one or more R¹ radicals, an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group, or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and is optionally substituted by one or more R¹ radicals; and wherein the R¹³ radical optionally defines a ring system with one or both of the R¹¹ and R¹² radicals.
 2. The composition of claim 1, wherein the Ar³ radical of formula (I) is substituted by Ar⁴ in at least one ortho position based on the position of the nitrogen atom shown in formula (I), wherein Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R radicals.
 3. The composition of claim 2, wherein the polymer comprises at least one structural unit of formula (I) selected from the structural unit of formula (Ia):

wherein q is 0, 1, 2, 3, 4, 5, or 6; X is CR₂, NR, SiR₂, O, S, C═O or P═O; and r is 0 or
 1. 4. The composition of claim 2, wherein Ar³ is substituted by Ar⁴ in one of the two ortho positions, and Ar³ is additionally joined to Ar⁴ in the meta position adjacent to the substituted ortho position.
 5. The composition of claim 2, wherein the polymer comprises at least one structural unit of formula (I) selected from the structural unit of formula (Ib):

wherein X is CR₂, NR, SiR₂, O, S, C═O, or P═O; m is 0, 1, 2, 3 or 4; n is 0, 1, 2, or 3; and s and t are each 0 or 1, wherein the sum of (s+t)=1 or
 2. 6. The composition of claim 2, wherein the at least one structural unit of formula (I) is selected from structural units of formulae (II), (III), and (IV):

wherein X is CR₂, NR, SiR₂, O, S, C═O, or P═O; m is 0, 1, 2, 3 or 4; n is 0, 1, 2, or
 3. 7. The composition of claim 6, wherein the at least one structural unit of formula (II) is selected from the structural unit of formula (V):

wherein p is 0, 1, 2, 3, 4, or
 5. 8. The composition of claim 6, wherein the at least one structural unit of formula (III) is selected from the structural unit of the following formula (VI):


9. The composition of claim 6, wherein the at least one structural unit of formula (IV) is selected from the structural unit of formula (VII):


10. The composition of claim 1, wherein the polymer comprises at least one structural unit of formula (I) selected from the structural unit of formula (VIIIa):

or the structural unit of formula (VIIIb):

wherein w is 1, 2, or 3; Ar⁵ to Ar⁹ are each the same or different at each instance and are a mono- or polycyclic, aromatic or heteroaromatic ring system optionally substituted by one or more R radicals; and the dotted lines denote bonds to adjacent structural units in the polymer.
 11. The composition of claim 10, wherein at least one of the Ar⁵ and/or Ar⁸ radicals of formulae (VIIIa) and/or (VIIIb) is substituted by Ar⁴ in at least one ortho position, based on the position of the nitrogen atom shown in formula (VIIIa) and/or (VIIIb), where Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R radicals.
 12. The composition of claim 10, wherein the at least one structural unit of formula (VIIIa) is selected from the structural units of formulae (VIIIa-1a), (VIIIa-1b), (VIIIa-1c), and (VIIIa-1d):

wherein Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R radicals; X is CR₂, NR, SiR₂, O, S, C═O, or P═O; m is 0, 1, 2, 3 or 4; n is 0, 1, 2, or 3; r is 0 or 1; and s and t are each 0 or 1, wherein the sum of (s+t)=1 or
 2. 13. The composition of claim 10, wherein the at least one structural unit of formula (VIIIa) is selected from structural units of formulae (IX), (X), (XI), (XII), (XIII), (XIV), (XV), and (XVI):

wherein Ar⁴ is a mono- or polycyclic, aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R radicals; X is CR₂, NR, SiR₂, O, S, C═O, or P═O; m is 0, 1, 2, 3 or 4; n is 0, 1, 2, or 3; and p is 0, 1, 2, 3, 4, or
 5. 14. The composition of claim 1, wherein at least one of the structural units of formulae (I) comprises at least one crosslinkable Q group.
 15. The composition of claim 1, wherein the mono- or polycyclic, aromatic or heteroaromatic Ar³ groups are selected from:

wherein X is CR₂, NR, SiR₂, O, S, C═O, or P═O; the dotted lines denote bonds to adjacent structural units in the polymer; m is 0, 1, 2, 3, or 4; n is 0, 1, 2, or 3; • is 0, 1, or 2; and p is 0, 1, 2, 3, 4, or
 5. 16. The composition of claim 1, wherein the mono- or polycyclic, aromatic or heteroaromatic Ar¹ and Ar² groups are selected from:

wherein X is CR₂, NR, SiR₂, O, S, C═O, or P═O; Y is CR₂, SiR₂, O, S, or a straight-chain or branched alkyl group having 1 to 20 carbon atoms or an alkenyl or alkynyl group having 2 to 20 carbon atoms, each of which is optionally substituted by one or more R¹ radicals, and wherein one or more nonadjacent CH₂ groups, CH groups, or carbon atoms in the alkyl, alkenyl, or alkynyl groups is optionally replaced by Si(R¹)₂, C═O, C═S, C═NR¹, P(═O)(R¹), SO, SO₂, NR, O, S, CONR¹, an aromatic or heteroaromatic ring system which has 5 to 60 aromatic ring atoms and is optionally substituted in each case by one or more R¹ radicals, an aryloxy or heteroaryloxy group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, an aralkyl or heteroaralkyl group which has 5 to 60 aromatic ring atoms and is optionally substituted by one or more R¹ radicals, or a diarylamino group, diheteroarylamino group, or arylheteroarylamino group which has 10 to 40 aromatic ring atoms and is optionally substituted by one or more R¹ radicals; the dotted lines represent bonds to adjacent structural units in the polymer; k is 0 or 1; m is 0, 1, 2, 3 or 4; n is 0, 1, 2 or 3; • s 0, 1 or 2; and q is 0, 1, 2, 3, 4, 5 or
 6. 17. The composition of claim 14, wherein the crosslinkable Q group is selected from the group consisting of (1) terminal or cyclic alkenyl or terminal dienyl and alkynyl groups, (2) alkenyloxy, dienyloxy, or alkynyloxy groups, (3) acrylic acid groups, (4) oxetane and oxirane groups, (5) silane groups, and (6) cyclobutane groups.
 18. The composition of claim 17, wherein the crosslinkable Q group is selected from:

wherein the R¹¹⁰, R¹²⁰ and R¹³⁰ radicals in the formulae Q1 to Q8, Q11, Q13 to Q20 and Q23 are the same or different at each instance and are H or a straight-chain or branched alkyl group having 1 to 6 carbon atoms; Ar¹⁰ in the formulae Q13 to Q 24 is a mono- or polycyclic, aromatic or heteroaromatic ring system which is optionally substituted by one or more R radicals; g is an integer from 0 to 8; h is an integer from 1 to 8; and the dotted bond in the formulae Q1 to Q11 and Q13 to Q23 and the dotted bonds in the formulae Q12 and Q24 denote the linkage of the crosslinkable group to one of the mono- or polycyclic, aromatic or heteroaromatic ring systems Ar^(l) to Ar³.
 19. The composition of claim 1, wherein the proportion of structural units of formulae (I) in the polymer is in the range from 1 to 100 mol %, based on 100 mol % of all copolymerized monomers present as structural units in the polymer.
 20. The composition of claim 1, wherein the polymer, as well as structural units of the formulae (I), comprises at least one further structural unit of formula (XIX) other than the structural units of formulae (I): —Ar¹¹—  (XII) wherein Ar¹¹ is a mono- or polycyclic, aromatic or heteroaromatic ring system optionally substituted by one or more R radicals.
 21. The composition of claim 14, wherein the proportion of structural units of the formula (I) having a crosslinkable Q group in the polymer is in the range from 0.1 to 50 mol %, based on 100 mol % of all copolymerized monomers present as structural units in the polymer.
 22. The composition of claim 1, wherein the R¹³ radical in formula (L-I) is selected from the group comprising alkyl, long-chain alkyl, alkoxy, long-chain alkoxy, cycloalkyl, haloalkyl, aryl, arylene, halogenaryl, heteroaryl, heteroarylene, heterocycloalkylene, heterocycloalkyl, haloheteroaryl, alkenyl, haloalkenyl, alkynyl, haloalkynyl, ketoaryl, haloketoaryl, ketoheteroaryl, ketoalkyl, haloketoalkyl, ketoalkenyl, haloketoalkenyl, wherein, in the case of suitable radicals, one or more nonadjacent CH₂ groups independently are optionally replaced by —O—, —S—, —NH—, —NR—, —SiR₂—, —CO—, —COO—, —OCO—, —OCO—O—, —SO₂—, —S—CO—, —CO—S—, —CR═CR— or —C≡C—, in such a way that oxygen and/or sulfur atoms are not bonded directly to one another, and are likewise optionally replaced by aryl or heteroaryl, wherein terminal CH₃ groups are regarded as CH₂ groups in the sense of CH₂—H.
 23. The composition of claim 1, wherein the metal atom of the metal complex is selected from the group comprising bismuth, tin, and mixtures thereof.
 24. The composition of claim 1, wherein the metal complex has the structure ML_(m) where M is a metal atom, L is a ligand, and m is an integer from 1 to 10 and, if m is greater than 1, all L are independent of one another.
 25. The composition of claim 1, wherein the R¹³ radical has at least one substituent selected from halogen, pseudohalogen, —CN, and —NO₂.
 26. The composition of claim 1, wherein the R¹³ radical corresponds to one of the formulae (R¹³-I), (R¹³-II), and (R¹³-III):

wherein the Y¹ to Y⁷ groups are each independently selected from the group comprising C—F, C—CF₃, C—NO₂, C—CN, C-halogen, C-pseudohalogen, and N.
 27. The composition of claim 1, wherein the metal complex comprises a ligand L selected from the group of the unsubstituted, partly fluorinated, and perfluorinated organic carboxylic acids.
 28. The composition of claim 1, wherein the weight ratio of polymer to metal complex is in the range from 1000:1 to 1:2.
 29. A process for producing a composition according claim 1, wherein a polymer having structural units of formula (I) is contacted with a metal complex comprising a metal atom of groups 13 to 15 and a ligand of the structure (L-I).
 30. A solution or formulation comprising at least one composition according to claim 1 in one or more solvents.
 31. An electronic or optoelectronic component comprising one or more active layers, wherein at least one of the one or more active layers comprises one or more compositions according to claim
 1. 32. The electronic or optoelectronic component of claim 31, wherein the electronic or optoelectronic component is selected from the group consisting of organic electroluminescent devices, organic light-emitting electrochemical cells, organic field-effect transistors, organic integrated circuits, organic thin-film transistors, organic solar cells, organic laser diodes, organic photovoltaic elements, organic photovoltaic devices, and organic photoreceptors.
 33. The electronic or optoelectronic component of claim 32, wherein the active layer comprising one or more compositions. 